Effects of hydroxyl-functionalization and sub-Tg thermal annealing on high pressure pure- and mixed-gas CO2/CH4 separation by polyimide membranes based on 6FDA and triptycene-containing dianhydrides

• Published in: Journal of membrane science Vol. 475 p.571-581; pp. 571 - 581
• Main Authors: Swaidan, Raja, Ghanem, Bader, Litwiller, Eric, Pinnau, I
• Format: Journal Article
• Language: English
• Published: 01.02.2015
• Subjects: adsorption; annealing; artificial membranes; carbon dioxide; cellulose acetate; fluorescence; heat; methane; microstructure; natural gas; permeability; polymers; sieving; solubility
• ISSN: 0376-7388
• DOI: 10.1016/j.memsci.2014.10.046

A sub-Tg thermally-annealed (250°C, 24h) ultra-microporous PIM-polyimide bearing a 9,10-diisopropyl-triptycene contortion center and hydroxyl-functionalized diamine (2,2-bis(3-amino-4-hydroxyphenyl)-hexafluoropropane, APAF) exhibited plasticization resistance up to 50bar for a 1:1 CO2/CH4 feed mixture, with a 9-fold higher CO2 permeability (30Barrer) and 2-fold increase in CO2/CH4 permselectivity (~50) over conventional dense cellulose acetate membranes at 10bar CO2 partial pressure. Interestingly, mixed-gas CO2/CH4 permselectivities were 10–20% higher than those evaluated under pure-gas conditions due to reduction of mixed-gas CH4 permeability by co-permeation of CO2. Gas transport, physisorption and fluorescence studies indicated a sieving pore-structure engaged in inter-chain charge transfer complexes (CTCs), similar to that of low-free-volume 6FDA–APAF polyimide. The isosteric heat of adsorption of CO2 as well as CO2/CH4 solubility selectivities varied negligibly upon replacement of OH with CH3 but CTC formation was hindered, CO2 sorption increased, CO2 permeability increased ~3-fold, CO2/CH4 permselectivity dropped to ~30 and CH4 mixed-gas co-permeation increased. These results suggest that hydroxyl-functionalization did not cause preferential polymer-gas interactions but primarily elicited diffusion-dominated changes owing to a tightened microstructure more resistant to CO2-induced dilations. Solution-processable hydroxyl-functionalized PIM-type polyimides provide a new platform of advanced materials that unites the high selectivities of low-free-volume polymers with the high permeabilities of PIM-type materials particularly for natural gas sweetening applications.