Surface modification of Ti-6Al-4V alloy by glow discharge-plasma nitriding

Titanium alloy (Ti-6Al-4V) samples were nitrided in low pressure (1.3, 3 mbar) dc-glow discharge plasmas of nitrogen. The treating time was 5, 10 and 15 hour and the temperatures range of the samples during the nitriding process was close to 800 oC. The obtained microstructures of the nitride layers...

Full description

Saved in:
Bibliographic Details
Published inIraqi Journal of Physics : a Refereed Journal Issued. Vol. 9; no. 16; pp. 34 - 40
Main Authors Khalaf, Muhammad Khammas, Jiyad, Baha Tumah, al-Ani, Zaynab Tariq, al-Zubaydi, Thair Latif Mazal
Format Journal Article
LanguageArabic
English
Published Baghdad, Iraq University of Baghdad, College of Science 01.12.2011
University of Baghdad
Subjects
Heat treatment
Nitriding
Plasma nitiding, DC-glow discharge, Titanium,Ti-6Al-4V
Surface hardening
Titanium alloys
Online AccessGet full text

Cover

More Information
Summary:Titanium alloy (Ti-6Al-4V) samples were nitrided in low pressure (1.3, 3 mbar) dc-glow discharge plasmas of nitrogen. The treating time was 5, 10 and 15 hour and the temperatures range of the samples during the nitriding process was close to 800 oC. The obtained microstructures of the nitride layers were studied by x-ray diffraction and optical microscopy. The ε–Ti2N, ζ-Ti3N3-x and η-Ti3N2-x.phases were formed and addition to the solid solution of nitrogen in titanium, α (Ti, N). Micro hardness measurements exhibit an increment for the Ti-alloy specimens which nitrided at 800oC for 10 and 15h.Corrosion measurements were obtained for the Ti-6Al-4V alloy in Ringer solution after plasma nitriding. The clear improving in the corrosion resistance was observed rather than for untreated specimens. في هذا البحث تمت معاملة عينات من سبيكة Ti-6Al-4V ببلازما النايتروجين بضغوط (3,1.3) ملي بار بمبدأ التفريغ التوهجي للتيار المستمر. أجريت المعاملة للعينات بزمن (15, 10, 5) ساعة و بدرجة حرارة تقريبا 800 درجة مئوية. التركيب البلوري لطبقات النترتة فحصت و شخصت باستخدام حيود الأشعة السينية و المجهر البصري. الأطوار المتشكلة هي η – Ti3N2-X, ζ - Ti3N3-X, ɛ-Ti2N بالإضافة إلى طور الصلب للنايتروجين في التيتانيوم (TiN) α. فحوصات الصلادة المايكورية أظهرت زيادة في المقدار لسبائك التيتانيوم المعاملة ببلازما (لمدة 10، 15 ساعة بدرجة 800 درجة مئوية). قياسات التآكل حصلت باستخدام محلول (Ringer) للعينات المعاملة بالبلازما و أظهرت وجود تحسس واضح في مقاومة التآكل للعينات المعاملة بالبلازما مقارنة مع العينات غير المعاملة.
ISSN:2070-4003
2664-5548