Synthesis of LiTiO2 Nanocrystals/Ordered Mesoporous Carbon Composite Hosts for High‐Performance Lithium–Sulfur Batteries

• Published in: Small science Vol. 3; no. 6
• Main Authors: Wang, Changyao, Zhang, Wei, Liu, Mengmeng, Duan, Linlin, Ma, Bing, Zhang, Xingmiao, Li, Wei
• Format: Journal Article
• Language: English
• Published: Weinheim John Wiley & Sons, Inc 01.06.2023; Wiley-VCH
• Subjects: Carbon; coassemblies; composites; Crystallization; Li–S batteries; mesoporous materials; Metal oxides; Microscopy; Nanocrystals; Particle size; Pore size; Spectrum analysis
• ISSN: 2688-4046; 2688-4046
• DOI: 10.1002/smsc.202300019

Metal oxide nanocrystals/mesoporous carbon composite materials are promising in the energy storage field. However, the construction of stoichiometric ternary nanocrystals‐functionalized mesoporous carbon materials remains a great challenge. Herein, the synthesis of ultradispersed and ultrasmall LiTiO2 nanocrystals/ordered mesoporous carbon composites via a chelation‐mediated multicomponent coassembly strategy is reported. In this case, the self‐assembly into ordered mesostructures and the crystallization of nanoparticle processes can be decoupled by the molecular chelate strategy where citrate ligands can effectively inhibit the hydrolysis and phase separation of metal oxide precursors and confine the crystallization into nanocrystals without aggregation. The obtained 33%‐LiTiO2–OMC composites present a high specific surface area (≈912 m2 g−1), a large pore volume (≈0.62 cm3 g−1), a uniform pore size (≈4.1 nm), and ultradispersed LiTiO2 nanocrystals (≈3 nm). When loading 60% sulfur, the composites exhibit a high reversible capacity (966 mAh g−1 after 100 cycles at 0.5C), an excellent rate capacity (700 mAh g−1 at 5C), and a long‐term cycling performance (63% retention after 1000 cycles at 5C). This method is very simple and reproducible, which paves a new way for the design and synthesis of functional mesoporous materials. A chelation‐mediated multicomponent coassembly strategy is developed for the controllable synthesis of ultradispersed and ultrasmall LiTiO2 nanocrystals/ordered mesoporous carbon composites with high specific surface areas, large pore volumes, and uniform pore size. When loading 60% sulfur, the composites exhibit a high reversible capacity, an excellent rate capacity, and a long‐term cycling performance.