The Effect of Scanning Strategy on the Thermal Behavior and Residual Stress Distribution of Damping Alloys during Selective Laser Melting

• Published in: Materials Vol. 17; no. 12; p. 2912
• Main Authors: Yan, Zhiqiang, Wu, Kaiwen, Xiao, Zhongmin, Hui, Jizhuang, Lv, Jingxiang
• Format: Journal Article
• Language: English
• Published: Basel MDPI AG 01.06.2024; MDPI
• Subjects: Additive manufacturing; Alloys; Cooling rate; Damping; damping alloy; Deformation; Efficiency; Finite element method; Heat; Impact strength; Influence; Interlayers; Laser beam melting; Lasers; Magnesium alloys; Melt pools; Metal industry; numerical modeling; Oxidation; Powder metallurgy; Powders; Residual stress; scanning strategy; selective laser melting; Simulation; Software; Stress concentration; Stress distribution; Temperature; thermal behavior; Thermodynamic properties
• ISSN: 1996-1944; 1996-1944
• DOI: 10.3390/ma17122912

The manufacture of damping alloy parts with stable damping properties and high mechanical performances in the selective laser melting (SLM) process is influenced by temperature evolution and residual stress distribution. Choosing an appropriate scanning strategy, namely the specific trajectory along which the laser head scans powders within given area, is crucial, but clearly defined criteria for scanning strategy design are lacking. In this study, a three-dimensional finite element model (FEM) of the SLM process for manufacturing a WE43 alloy component was established and validated against the published experimental data. Eleven different scanning strategies were designed and simulated, considering variables such as scanning track length, direction, Out–In or In–Out strategy, start point, and interlayer variation. The results showed that scanning strategy, geometry, and layer number collectively affect temperature, melt pool, and stress outputs. For instance, starting scanning at a colder part of the powder layer could lead to a high peak temperature and low melt pool depth. A higher layer number generally results in lower cooling rate, a lower temperature gradient, a longer melt pool life, and larger melt pool dimensions. Changing the start point between scanning circulations helps mitigate detrimental residual stress. This work highlights the potential of analyzing various scanning strategy-related variables, which contributes to reducing trial-and-error tests and selecting optimal scanning strategies under different product quality requirements. This article can assist in the design of appropriate scanning strategies to prevent defects such as element loss due to evaporation, poor bonding, and deformation or cracking from high residual stress. Additionally, identifying stress concentration locations and understanding the effects of geometry and layer number on thermal and mechanical behaviors can assist in geometry design.