One-Step Synthesis of Selective Nife-Layered Double Hydroxide Anode Catalyst for Highly Efficient and Stable Anion Exchange Membrane Water Electrolyzers, Operating with Seawater

• Published in: Meeting abstracts (Electrochemical Society) Vol. MA2022-02; no. 39; p. 1389
• Main Authors: Xing, Jiale, Zeng, Zhiqiao, Koni, Arkid, Mirshekari, Gholamreza, Best, Wesley, Kumar, Vikas, Sammes, Lauren, Bonville, Leonard J., Maric, Radenka, Bliznakov, Stoyan
• Format: Journal Article
• Language: English
• Published: The Electrochemical Society, Inc 09.10.2022
• ISSN: 2151-2043; 2151-2035
• DOI: 10.1149/MA2022-02391389mtgabs

Seawater electrolysis faces unique and fundamental chemical challenges, such as the suppression of highly detrimental halogen chemistries [1], that poison the current state-of-the-art anode catalyst and accelerate the degradation of the membrane [2]. The technically favored solution path is to address these issues by developing a new selective catalyst and possibly by limiting operating conditions [3]. Therefore, developing a facile and cost-effective way to design highly active, selective, and and stable seawater-splitting catalysts is of great importance for research and industry [4]. In this work, hexagonal NiFe-layered double hydroxide (LDH) nanosheets were synthesized by one-step solvothermal reactions. As synthesized NiFe-LDH catalyst exhibits high activity, selectivity, and stability towards the oxygen evolution reaction (OER) in alkaline electrolyte, delivering current densities of 10 mA/cm 2 at low overpotentials of 359 mV, with no significant degradation observed during RDE testing at constant voltage of 1.57 V for 72 hours in 1.0 M KOH electrolyte. In addition, in order to fabricate catalyst coated electrode (CCE), the nanostructured NiFe-LDH catalyst was homogeneously sprayed onto a platinized titanium porous transport layer (PTL) using an ultrasonic spray coating system. As prepared CCE is used as an anode and commercially available Raney nickel catalyst deposited on a nickel fiber frit is used as a cathode to assemble a MEA with Sustainion ® X37-50 grade T anion exchange membrane (AEM) that was tested in alkaline seawater. Employing local seawater, the AEM electrolyzer cell demonstrated stable performance for over 1000 hours at a constant current density of 300 mA cm -2 . Reference: [1] S.-C. Ke, R. Chen, G.-H. Chen, X.-L. Ma, Energy Fuels 2021, 35 , 12948. [2] S. Dresp, F. Luo, R. Schmack, S. Kühl, M. Gliech, P. Strasser, Energy Environ. Sci. 2016, 9 , 2020. [3] S. Dresp, F. Dionigi, S. Loos, J. Ferreira de Araujo, C. Spöri, M. Gliech, H. Dau, P. Strasser, Advanced Energy Materials 2018, 8 , 1800338. [4] H. Koshikawa, H. Murase, T. Hayashi, K. Nakajima, H. Mashiko, S. Shiraishi, Y. Tsuji, ACS Catal. 2020, 10 , 1886.