Non defect-stabilized thermally stable single-atom catalyst

• Published in: Nature communications Vol. 10; no. 1; p. 234
• Main Authors: Lang, Rui, Xi, Wei, Liu, Jin-Cheng, Cui, Yi-Tao, Li, Tianbo, Lee, Adam Fraser, Chen, Fang, Chen, Yang, Li, Lei, Li, Lin, Lin, Jian, Miao, Shu, Liu, Xiaoyan, Wang, Ai-Qin, Wang, Xiaodong, Luo, Jun, Qiao, Botao, Li, Jun, Zhang, Tao
• Format: Journal Article
• Language: English
• Published: London Nature Publishing Group UK 16.01.2019; Nature Publishing Group; Nature Portfolio
• Subjects: 140/146; 147/137; 639/638/563/979; 639/638/77/887; 639/925/357/551; Humanities and Social Sciences; Information processing; Invariance; multidisciplinary; Odors; Olfactory bulb; Olfactory stimuli; Perception; Science; Science (multidisciplinary); Single atom catalysts; Smell
• ISSN: 2041-1723; 2041-1723
• DOI: 10.1038/s41467-018-08136-3

Surface-supported isolated atoms in single-atom catalysts (SACs) are usually stabilized by diverse defects. The fabrication of high-metal-loading and thermally stable SACs remains a formidable challenge due to the difficulty of creating high densities of underpinning stable defects. Here we report that isolated Pt atoms can be stabilized through a strong covalent metal-support interaction (CMSI) that is not associated with support defects, yielding a high-loading and thermally stable SAC by trapping either the already deposited Pt atoms or the PtO 2 units vaporized from nanoparticles during high-temperature calcination. Experimental and computational modeling studies reveal that iron oxide reducibility is crucial to anchor isolated Pt atoms. The resulting high concentrations of single atoms enable specific activities far exceeding those of conventional nanoparticle catalysts. This non defect-stabilization strategy can be extended to non-reducible supports by simply doping with iron oxide, thus paving a new way for constructing high-loading SACs for diverse industrially important catalytic reactions. Developing stable single-atom catalysts (SACs) with a high metal loading remains a challenge due to the difficulty of creating high densities of defects on support materials. Here the authors prepare Pt SACs with high Pt loadings by virtue of strong covalent metal-support interaction, rather than support defects.