碱熔融-电感耦合等离子体发射光谱法测定高硫铝土矿中的硫

应用电感耦合等离子体发射光谱法（ICP-OES）测定高硫铝土矿（硫含量≤8%）中的硫时,由于硫存在-2、＋4和＋6等多种价态,常用的酸溶法和碱熔法处理高硫铝土矿时往往无法完全氧化硫而导致硫测定结果偏低。本文用过氧化钠熔融、热水浸取和盐酸酸化提取高硫铝土矿中的硫,使用基体匹配法绘制校准曲线补偿铝和钠对硫测定的光谱干扰,以S182.034 nm（184 nm）作为分析谱线,采用ICP-OES对硫进行测定。结果表明：3 g过氧化钠在700℃下熔融10 min,可以较好地氧化高硫铝土矿中的硫;校准曲线的线性相关系数为0.9999,方法检出限为0.025μg/m L,相对标准偏差（RSD,n=6）小于5...

Full description

Saved in:
Bibliographic Details
Published in岩矿测试 Vol. 36; no. 2; pp. 124 - 129
Main Author 胡璇 石磊 张炜华
Format Journal Article
LanguageChinese
Published 国家轻金属质量监督检验中心,河南 郑州,450041 2017
Subjects
电感耦合等离子体发射光谱法
硫
过氧化钠碱熔
铝土矿
sodium peroxide fusion
铝土矿
Inductively Coupled Plasma-Optical Emission Spectrometry
电感耦合等离子体发射光谱法
bauxite
sulfur
硫
过氧化钠碱熔
Online AccessGet full text

Cover

More Information
Summary:应用电感耦合等离子体发射光谱法（ICP-OES）测定高硫铝土矿（硫含量≤8%）中的硫时,由于硫存在-2、＋4和＋6等多种价态,常用的酸溶法和碱熔法处理高硫铝土矿时往往无法完全氧化硫而导致硫测定结果偏低。本文用过氧化钠熔融、热水浸取和盐酸酸化提取高硫铝土矿中的硫,使用基体匹配法绘制校准曲线补偿铝和钠对硫测定的光谱干扰,以S182.034 nm（184 nm）作为分析谱线,采用ICP-OES对硫进行测定。结果表明：3 g过氧化钠在700℃下熔融10 min,可以较好地氧化高硫铝土矿中的硫;校准曲线的线性相关系数为0.9999,方法检出限为0.025μg/m L,相对标准偏差（RSD,n=6）小于5%;与碳硫仪的测定结果相比较,两种方法无显著性差异。本方法溶样彻底,无样品损失,为今后实现应用ICP-OES同时测定高硫铝土矿中的硫和其他元素奠定了基础。
Bibliography:bauxite; sulfur; sodium peroxide fusion; Inductively Coupled Plasma-Optical Emission Spectrometry
When Inductively Coupled Plasma-Optical Emission Spectrometry （ ICP-OES） is used to analyze the sulfur content of high-sulfur （ S≤ 8% ） bauxite,commonly used acid dissolving and alkali fusion methods cannot oxidize sulfur completely, leading to a false （lower） result of sulfur due to multiple valences of sulfur （-2 , ＋ 4 ,＋ 6 ） . In this study,high-sulfur bauxite samples were fused with sodium hydroxide and leached out by hot water and hydrochloricacid,and the calibration curve was plotted through a matrix matching method to compensate for the spectralinterferences of aluminum and sodium on sulfur. S182.034 nm （184 nm） was selected as the analytical line, andsulfur was analyzed by ICP-OES. Results show that sulfur in high-sulfur bauxite samples is completely oxidized with 3 g sodium peroxide at 700℃ for 10 min. The linear correlation coefficient of the calibration curve was 0. 9999 ,the detection limit was 0.025 μ
ISSN:0254-5357
DOI:10.15898/j.cnki.11-2131/td.2017.02.005