The Wear and Tear of Teeth

• Published in: Medical principles and practice Vol. 24; no. Suppl 1; pp. 3 - 13
• Main Authors: Lucas, Peter W., van Casteren, Adam
• Format: Journal Article
• Language: English
• Published: Basel, Switzerland S. Karger AG 01.01.2015
• Subjects: Bicuspid - pathology; Biomechanical Phenomena; Cuspid - pathology; Dental Enamel - pathology; Dental Enamel - ultrastructure; Dental Stress Analysis; Fractures, Stress - pathology; Humans; Incisor - pathology; Molar - pathology; Review; Stress, Mechanical; Surface Properties; Tooth - pathology; Tooth - ultrastructure; Tooth Fractures - pathology; Tooth Wear - pathology; Tooth enamel; Tooth fracture; Mechanical damage
• ISBN: 9783318030204; 3318030201
• ISSN: 1011-7571; 1423-0151; 1423-0151
• DOI: 10.1159/000367976

A review is presented of the mechanical damage suffered by tooth crowns. This has been the subject of much recent research, resulting in a need to revise some of the thinking about the mechanisms involved. Damage is classified here by scale into macro-, meso- and microfracture. The focus is on the outer enamel coat because this is the contact tissue and where most fractures start. Enamel properties appear to be tailored to maximize hardness, but also to prevent fracture. The latter is achieved by the deployment of developmental flaws called enamel tufts. Macrofractures usually appear to initiate as extensions of tufts on the undersurface of the enamel adjacent to the enamel-dentine junction and extend from there into the enamel. Cracks that pass from the tooth surface tend to be deflected by an enamel region of high toughness; if they find the surface again, a chip (mesofracture) is produced. The real protection of the enamel-dentine junction here is the layer of decussating inner enamel. Finally, a novel analysis of mechanical wear (microfracture) suggests that the local toughness of the enamel is very important to its ability to resist tissue loss. Enamel and dentine have contrasting behaviours. Seen on a large scale, dentine is isotropic (behaving similarly in all directions) while enamel is anisotropic, but vice versa on a very small scale. These patterns have implications for anyone studying the fracture behaviour of teeth.