Bonding Performance of a Hydrophilic Amide Monomer Containing Adhesive to Occlusal and Cervical Dentin

• Published in: Materials Vol. 13; no. 21; p. 4727
• Main Authors: Seitoku, Eri, Hoshika, Shuhei, Ikeda, Takatsumi, Abe, Shigeaki, Tanaka, Toru, Sano, Hidehiko
• Format: Journal Article
• Language: English
• Published: Basel MDPI AG 23.10.2020; MDPI
• Subjects: Adhesion; Adhesives; Aqueous solutions; Bond strength; Bonding strength; Composite materials; Dentin; failure modes; hydrophilic amide monomer; Hydrophilicity; Interfaces; microtensile bond strength; Monomers; Performance evaluation; scanning electron microscope; Silicon carbide; Teeth; Variance analysis; Water storage; Japan
• ISSN: 1996-1944; 1996-1944
• DOI: 10.3390/ma13214727

This study aimed to evaluate the bonding performance of a new one-step self-etching adhesive system containing a novel hydrophilic amide monomer. Clearfil Universal Bond Quick (CUB) and Clearfil Megabond 2 (CMB) were used as the one-step and two-step adhesive systems, respectively. Flat dentin surfaces of human premolars were exposed using #600 SiC (silicon carbide) and bonded with the respective adhesives of each system. The teeth were sectioned to obtain beams (1 mm × 1 mm) after 24 h of water storage. The mean bond strength and standard deviations (MPa) on an occlusal surface were as follows: CUB: 45.9 ± 19.7 and CMB: 67.9 ± 25.3. The values for cervical ones were CUB: 56.0 ± 20.3 and CMB: 67.6 ± 16.0, respectively. In both conditions, the microtensile bond strength (μTBS) value was lower than that of CMB. As seen during the microscopic observation, no adhesive failure was observed after μTBS testing because CUB formed a firm and tight adhesive interface.