In vitro fracture resistance of posterior metal-ceramic and all-ceramic inlay-retained resin-bonded fixed partial dentures

• Published in: The Journal of prosthetic dentistry Vol. 92; no. 4; pp. 365 - 370
• Main Authors: Kılıçarslan, Mehmet A., Sema Kedici, P., Cenker Küçükeşmen, H., Uludağ, Bülent C.
• Format: Journal Article
• Language: English
• Published: United States Mosby, Inc 01.10.2004
• Subjects: Ceramics; Compressive Strength; Dental Materials; Dental Prosthesis Retention; Dental Stress Analysis - methods; Dentistry; Denture Design; Denture, Partial, Fixed, Resin-Bonded; Humans; Lithium Compounds; Materials Testing - methods; Metal Ceramic Alloys; Zirconium
• ISSN: 0022-3913; 1097-6841
• DOI: 10.1016/j.prosdent.2004.07.001

Inlay-retained resin-bonded fixed partial dentures (RBFPDs) are conservative prosthetic restorations; however, their resistance to fracture is not clear. The purpose of this study was to compare fracture loads of posterior complete coverage metal-ceramic restorations with all-ceramic inlay-retained RBFPDs. Thirty-two posterior ceramic RBFPD restorations were divided into 4 groups (n=8): (1) Complete metal-ceramic fixed partial dentures (MC-FPDs) fabricated of Ni-Cr–based alloy (Wirolloy) and veneered with a ceramic (IPS d.SIGN) as the control group; (2) inlay-retained metal-ceramic (MC RBFPDs) with the same materials as the control; (3) inlay-retained lithium disilicate (LD) glass-ceramic (IPS Empress 2) RBFPDs; and (4) inlay-retained zirconia-based (Z) ceramic (Cercon) RBFPDs. Control specimens were prepared to receive conventional complete MC-FPDs designed to include a 1.3-mm-circumferential, 90-degree flat shoulder with rounded angles. Inlay-retained RBFPD specimens were prepared with 2-mm occlusal reduction but without bevels at the occlusal or gingival margins. Specimens were loaded and fracture loads (N) measured at fracture with a universal testing machine at a crosshead speed of 1.0 mm/min and 250 kgf load cell. Data were analyzed with 1-way ANOVA and Duncan test (α=.001). Fracture loads (mean ± SD) were greatest for control specimens (1318.43 ± 211.00 N) and Z-RBFPD (1247.70 ± 262.51 N) specimens as compared to MC-RBFPD or LD-RBFPD ( P<.001). MC-RBFPD exhibited the next highest fracture loads (958.01 ± 194.29 N), and LD-RBFPD exhibited the significantly lowest values (303.23 ± 92.54 N) of the materials tested ( P<.001). Inlay-retained zirconia-based ceramic RBFPDs demonstrated the greatest fracture resistance among all inlay-retained restorations tested.