Impact of Ultraviolet Radiation on the Aging Properties of SBS-Modified Asphalt Binders

• Published in: Polymers Vol. 11; no. 7; p. 1111
• Main Authors: Yu, Huanan, Bai, Xianping, Qian, Guoping, Wei, Hui, Gong, Xiangbing, Jin, Jiao, Li, Zhijie
• Format: Journal Article
• Language: English
• Published: Switzerland MDPI AG 01.07.2019; MDPI
• Subjects: Aging; Asphalt pavements; Binders (materials); Butadiene; cracking; Crosslinking; Degradation; Fatigue strength; Fracture mechanics; functional group; Functional groups; Laboratories; Low temperature; Low temperature resistance; NMR; Nuclear magnetic resonance; Pavement design; Rheological properties; Rheology; Roads & highways; SBS-modified asphalt binder; Service life; Spectrum analysis; Styrenes; Systems analysis; Test methods; Thin films; Ultraviolet radiation; UV aging; China; UV aging; functional group; SBS-modified asphalt binder; rheological properties; cracking
• ISSN: 2073-4360; 2073-4360
• DOI: 10.3390/polym11071111

Styrene Butadiene Styrene (SBS) polymer-modified asphalt binders have become widely used in asphalt pavement because of their advantages in high- and low-temperature performance and fatigue resistance. Asphalt pavement is inevitably exposed to sunlight and ultraviolet (UV) radiation during its construction and service life. However, consideration of the aging effect of UV radiation is still limited in current pavement design and evaluation systems. In order to evaluate the impact of UV radiation on the aging properties of SBS-modified asphalt binders, UV aging tests were performed on Rolling Thin Film Oven Test (RTFOT)-aged samples with different UV radiation intensities and aging times. Sixteen different groups of tests were conducted to compare the rheological properties and functional group characteristics of SBS-modified asphalt binders. Dynamic Shear Rheometer (DSR), Bending Beam Rheometer (BBR), FTIR, and SEM tests were conducted to evaluate the aging mechanisms in various UV aging conditions. The results found that UV radiation seriously destroys the network structure formed by the cross-linking effect in SBS-modified asphalt binders, which aggravates the degradation of SBS and results in a great change of rheological properties after UV aging. The nature of SBS-modified asphalt binder aging resulted from the degradation of SBS and the changes of asphalt binder base composition, which lead to the transformation of colloidal structure and the deterioration of asphalt binder performance. The tests also found that continuous UV radiation can increase shrinkage stress in the asphalt binder surface and leads to surface cracking of the asphalt binder.