The influence of cement mantle thickness and stem geometry on fatigue damage in two different cemented hip femoral prostheses

• Published in: Journal of biomechanics Vol. 42; no. 15; pp. 2602 - 2610
• Main Authors: Ramos, A, Simões, J.A
• Format: Journal Article
• Language: English
• Published: United States Elsevier Ltd 13.11.2009; Elsevier Limited
• Subjects: Adhesiveness; Cement; Cementation - methods; Cemented stem; Crack initiation; Equipment Failure Analysis; Fatigue; Femur - physiopathology; Femur - surgery; Geometry; Hip Prosthesis; Humans; In vitro fatigue tests; Physical Medicine and Rehabilitation; Prosthesis Design; Strain gauges; Studies; Success; Synthetic femur; Transplants & implants; In vitro fatigue tests; Synthetic femur; Cemented stem; Crack initiation
• ISSN: 0021-9290; 1873-2380
• DOI: 10.1016/j.jbiomech.2009.06.037

Abstract Experimental models can be used for pre-clinical testing of cemented and other type of hip replacements. Total hip replacement (THR) failure scenarios include, among others, cement damage accumulation and the assessment of accurate stress and strain magnitudes at the cement mantle interfaces (stem-cement and cement-bone) can be used to predict mechanical failure. The aseptic loosening scenario in cemented hip replacements is currently not fully understood, and methods of evaluating medical devices must be developed to improve clinical performance. Different results and conclusions concerning the cement micro-cracking mechanism have been reported. The aim of this study was to verify the in vitro behavior of two cemented femoral stems with respect to fatigue crack formation. Fatigue crack damage was assessed at the medial, lateral, anterior and posterior sides of the Lubinus SPII and Charnley stems. All stems were loaded and tested in stair climbing fatigue loading during one million cycles at 2 Hz. After the experiments each implanted synthetic femur was sectioned and analyzed. We observed more damage (cracks per area) for the Lubinus SPII stem, mainly on the proximal part of the cement mantle. The micro-cracking formation initiated in the stem–cement interface and grew towards the direction of cortical bone of the femur. Overall, the cement–bone interface seems to be crucial for the success of the hip replacement. The Charnley stem provoked more damage on the cement–bone interface. A failure index (maximum length of crack/maximum thickness of cement) considered was higher for the cement–stem interface of the Lubinus SPII stem. For a cement mantle thickness higher than 5 mm, cracking initiated at the cement–bone interface and depended on the opening canal process (reaming procedure and instrumentation). The analysis also showed that fatigue-induced damage on the cement mantle, increasing proximally, and depended on the axial position of the stem. The cement thickness is an important factor for the success of THR and this study evidenced that cement thickness higher than 2 mm apparently does not affect the mechanical behavior of the cement mantel and induce more crack formation on the cement–bone interface.