Structural Evolution in Isothermal Crystallization Process of Poly(L-lactic acid) Enhanced by Silk Fibroin Nano-Disc

• Published in: Materials Vol. 12; no. 11; p. 1872
• Main Authors: Pandey, Amit Kumar, Katiyar, Vimal, Takagi, Hideaki, Shimizu, Nobutaka, Igarashi, Noriyuki, Sasaki, Sono, Sakurai, Shinichi
• Format: Journal Article
• Language: English
• Published: Switzerland MDPI AG 10.06.2019; MDPI
• Subjects: Acids; Crystal structure; crystalline lamella; Crystallinity; Crystallites; Crystallization; Degree of crystallinity; Impact strength; isothermal crystallization; Lamella; lamellar stacking; Mechanical properties; Nucleation; poly(L-lactic acid); Polylactic acid; Polymers; Polymorphism; Silk fibroin; silk fibroin nano-disc; small-and wide-angle X-ray scattering simultaneous measurement; Synchrotrons; Thickening; X-ray scattering; Japan; small-and wide-angle X-ray scattering simultaneous measurement; isothermal crystallization; silk fibroin nano-disc; poly(L-lactic acid); crystalline lamella; lamellar stacking
• ISSN: 1996-1944; 1996-1944
• DOI: 10.3390/ma12111872

The nucleating effect of silk fibroin nano-disc (SFN) on the crystallization behavior of poly(L-lactic acid) (PLLA) was investigated by simultaneous synchrotron small- and wide-angle X-ray scattering measurements. For the isothermal crystallization at 110 °C from the melt, the induction period of the PLLA specimens containing 1% SFN was reduced compared to that of the neat specimens, indicating the acceleration of the nucleation of PLLA. The final degree of crystallinity was also increased, and the crystallization half-time was decreased, which indicates that the overall crystallization process was accelerated. Furthermore, the final value of the crystallite size (the lateral size of the crystalline lamella) was slightly lower for the specimens containing 1% SFN than that for the PLLA neat specimen, although the crystallites started growing much earlier. However, it was found that there was no effect of SFN on the growth rate of the crystallite size. The lamellar thickening process was also accelerated with a clear overshooting phenomenon with the inclusion of 1% SFN. As for the polymorphism, the α' phase is dominant with about 96%, but a small amount of the α phase (4%) is found to exist. It was found that the SFN can also accelerate the formation of the minor α phase as well as the major α' phase.