Wear of Polymer-Infiltrated Ceramic Network Materials against Enamel

• Published in: Materials Vol. 15; no. 7; p. 2435
• Main Authors: Tokunaga, Jumpei, Ikeda, Hiroshi, Nagamatsu, Yuki, Awano, Shuji, Shimizu, Hiroshi
• Format: Journal Article
• Language: English
• Published: Switzerland MDPI AG 25.03.2022; MDPI
• Subjects: Behavior; ceramic; Ceramics; Clinical medicine; Composite materials; crown; Dental materials; Dental restorative materials; Diamond pyramid hardness tests; Enamel; Lithium; Mechanical properties; Microstructure; PICN; Polymers; restorative materials; Teeth; Wear tests; Zirconium dioxide; Japan; ceramic; PICN; restorative materials; mechanical properties; dental materials; crown
• ISSN: 1996-1944; 1996-1944
• DOI: 10.3390/ma15072435

Polymer-infiltrated ceramic network materials (PICNs) have high mechanical compatibility with human enamel. However, the wear properties of PICN against natural human enamel have not yet been clarified. We investigated the in vitro two-body wear behaviors of PICNs and an enamel antagonist. Two PICNs were used: Experimental PICN (EXP) prepared via the infiltration of methacrylate-based resin into the porous silica ceramic network and commercial Vita Enamic (ENA). Two commercial dental ceramics, lithium disilicate glass (LDS) and zirconia (ZIR), were also characterized, and their wear performance was compared to PICNs. The samples were subjected to Vickers hardness tests and two-body wear tests that involve the samples being cyclically impacted by enamel antagonists underwater at 37 °C. The results reveal that the Vickers hardness of EXP (301 ± 36) was closest to that of enamel (317 ± 17). The volumetric wear losses of EXP and ENA were similar to those of LDS but higher than that of zirconia. The volumetric wear loss of the enamel antagonist impacted against EXP was moderate among the examined samples. These results suggest that EXP has wear behavior similar to that of enamel. Therefore, PICNs are mechanically comparable to enamel in terms of hardness and wear and are excellent tooth-restoration materials.