Role of boron carbide in carbothermic formation of hexagonal boron nitride

• Published in: Journal of materials science Vol. 41; no. 15; pp. 4921 - 4927
• Main Authors: CAMURLU, H. E, SEVINC, N, TOPKAYA, Y
• Format: Journal Article
• Language: English
• Published: Heidelberg Springer 01.08.2006; Springer Nature B.V
• Subjects: Activated carbon; Applied sciences; Argon; Atmospheres; Boron; Boron carbide; Boron nitride; Boron oxide; Boron oxides; Building materials. Ceramics. Glasses; Carbothermic reactions; Ceramic industries; Ceramics industry; Chemical analysis; Chemical industry and chemicals; Exact sciences and technology; Experiments; Materials science; Miscellaneous; Mixed oxides; Organic chemistry; Reaction products; Scanning electron microscopy; Silicones; Technical ceramics; X ray powder diffraction; X-ray diffraction; Scanning electron microscopy; Hexagonal lattices; Carbothermy; Boron nitride; Technical ceramics; Manufacturing; Experimental study; X ray diffraction; Formation mechanism; Precursor; Boron carbide; Non oxide ceramics
• ISSN: 0022-2461; 1573-4803
• DOI: 10.1007/s10853-006-0339-6

Formation of hexagonal boron nitride by carbothermic reduction of boric oxide under nitrogen atmosphere at 1500 °C was investigated. Experiments were performed for durations in the range of 15 min to 3 h. Reaction products were subjected to powder X-ray diffraction analysis, chemical analysis and were examined by scanning electron microscope. Formation of hexagonal boron nitride was found to be complete in 3 h with most forming in the initial 2 h. Boron carbide was found to exist in the reaction products of the experiments in which hexagonal boron nitride formation was not complete. The aim of this study was to investigate the role of boron carbide in the carbothermic production of hexagonal boron nitride. For this purpose, conversion reaction of boron carbide into hexagonal boron nitride was studied. Boron carbide used in these experiments was produced in the same conditions that hexagonal boron nitride was formed, but under argon atmosphere. It was found that formation of hexagonal boron nitride from boron carbide—boric oxide mixtures was slower than activated carbon—boric oxide mixtures. It was concluded that boron carbide is not a necessary intermediate product in the carbothermic production of hexagonal boron nitride.