Modification of surface properties of high and low density polyethylene by Ar plasma discharge

• Published in: Polymer degradation and stability Vol. 91; no. 6; pp. 1219 - 1225
• Main Authors: Švorčík, V., Kolářová, K., Slepička, P., Macková, A., Novotná, M., Hnatowicz, V.
• Format: Journal Article
• Language: English
• Published: Oxford Elsevier Ltd 01.06.2006; Elsevier Science
• Subjects: Ablation; Applied sciences; Chemical structure and surface morphology modification; Coating, metallization, dyeing; Exact sciences and technology; Low and high density polyethylene; Machinery and processing; Plasma discharge; Plastics; Polymer industry, paints, wood; Technology of polymers; Chemical structure and surface morphology modification; Low and high density polyethylene; Plasma discharge; Ablation; High density ethylene polymer; Roughness; Plasma assisted processing; Experimental study; Property processing relationship; Surface treatment; Surface structure; Structure processing relationship; Low density ethylene polymer; Morphology; Surface properties; Olefin polymer; Oxidation
• ISSN: 0141-3910; 1873-2321
• DOI: 10.1016/j.polymdegradstab.2005.09.007

Structural changes induced by Ar plasma discharge in low and high density polyethylene (LDPE and HDPE) were studied by different techniques. AFM and SEM methods were used to determine surface morphology, the changes in chemical structure were followed using FTIR and UV–vis spectroscopy. The content and the depth profile of incorporated oxygen was determined by RBS method. The degree of polymer ablation was determined gravimetrically. Standard goniometry was used to determine contact angle and to follow aging of plasma modified polymer. As a result of plasma treatment a lamellar structure or spherulites appear on the surface of HDPE and LDPE, respectively. Pronounced increase of the surface roughness is observed on HDPE contrary to LDPE. Plasma treatment for 400 s leads to the ablation of the surface layer of about 0.6 and 1 μm thick for LDPE and HDPE, respectively. Plasma treatment results in oxidation of the polymer surface layer which is more pronounced in HDPE. Concentration maximum of incorporated oxygen lies 25 nm beneath the sample surface in both polymer types. After exposure to plasma discharge carbonyl, carboxyl and amide groups were detected in the polymer surface layer together with C C bonds either in aromatic or in aliphatic structures. Immediately after the plasma treatment strong decline of the contact angle is observed, the decline being larger in HDPE. Later, in aged specimens the contact angle increases rapidly. The increase, which may be due to rearrangement of degraded structures, is stronger in the specimens exposed to plasma for longer times.