Sonically modified hierarchical FAU-type zeolites as active catalysts for the production of furan from furfural

• Published in: Ultrasonics sonochemistry Vol. 60; p. 104785
• Main Authors: Kuterasiński, Łukasz, Rojek, Wojciech, Gackowski, Mariusz, Zimowska, Małgorzata, Jodłowski, P.J.
• Format: Journal Article
• Language: English
• Published: Netherlands Elsevier B.V 01.01.2020
• Subjects: Desilication; Faujasite; Furan; Furfural; Mesoporosity; Sonochemistry; Furan; Desilication; Furfural; Sonochemistry; Mesoporosity; Faujasite
• ISSN: 1350-4177; 1873-2828
• DOI: 10.1016/j.ultsonch.2019.104785

•Zeolite desilication is independent on the presence of ultrasounds.•The application of ultrasounds improves mesoporosity in prepared zeolites.•Sonochemically treated hierarchical zeolites improves catalytic activity if furfural decarbonylation.•The effect of ultrasonic irritation decreased with increasing TBAOH content. In this study, the sonochemical-assisted desilication method was applied as a special and innovative way of preparing hierarchical zeolites. The physicochemical properties of the hierarchical zeolites prepared using the sonochemical route were compared with those prepared using the conventional desilication method. Commercial zeolite with FAU-type structure was desilicated with a sodium and tetrabutylammonium hydroxide aqueous solution (NaOH/TBAOH) for 30 min. The ultrasound treatment process was performed using a QSonica Q700 sonicator (Church Hill Rd, Newtown, CT, USA) equipped with a ½″ diameter horn. The average power of sonication was 60 W, and the frequency was 20 kHz. During the sonication procedure, the alkaline solution with the catalyst precursor and sonicator probe were placed in an ice bath to keep them at room temperature. The prepared catalyst samples were examined by ICP-OES, XRD, SEM, NMR, and nitrogen sorption techniques. The acidic properties of the prepared hierarchical zeolite samples were assessed by means of IR spectroscopy with ammonia and carbon monoxide sorption as probe molecules. All catalysts were studied in the decarbonylation of furfural into furan. Independently of the application of ultrasonic irradiation, desilication of zeolites with an NaOH/TBAOH mixture extracts comparable amounts of silicon, resulting in comparable crystallinity and acidity. On the other hand, the samples prepared in the presence of ultrasounds revealed higher both mesoporosity and enhanced catalytic properties in the reaction of decarbonylation of furfural into furan in comparison with their counterparts prepared using the conventional method.