Preparation and Gas-Sensing Properties of Two-Dimensional Molybdenum Disulfide/One-Dimensional Copper Phthalocyanine Heterojunction

• Published in: Sensors (Basel, Switzerland) Vol. 23; no. 23; p. 9321
• Main Authors: Chen, Guoqing, Xu, Xiaojie, Wang, Hao, Shaymurat, Talgar
• Format: Journal Article
• Language: English
• Published: Switzerland MDPI AG 22.11.2023
• Subjects: Air quality management; Composite materials; Copper; CuPc; Ethanol; gas sensor; Gases; heterojunction; Molybdenum; MoS2; Nanoparticles; Nanowires; Nitrogen oxide; Outdoor air quality; Phthalocyanins; Ratios; Research methodology; Sensors; Silicon wafers; Sulfur compounds; Temperature; VOC; VOCs; Volatile organic compounds; gas sensor; VOC; CuPc; MoS2; ethanol; heterojunction
• ISSN: 1424-8220; 1424-8220
• DOI: 10.3390/s23239321

Although 2D MoS2 alone shows excellent gas-sensing performance, it is prone to stacking when used as the sensitive layer, resulting in insufficient contact with the target gas and lower sensitivity. To solve this, a 2D-MoS2/1D-CuPc heterojunction was prepared with different weight ratios of MoS2 nanosheets to CuPc micro-nanowires, and its room-temperature gas-sensing properties were studied. The response of the 2D-MoS2/1D-CuPc heterojunction to a target gas was related to the weight ratio of MoS2 to CuPc. When the weight ratio of MoS2 to CuPc was 20:7 (7-CM), the gas sensitivity of MoS2/CuPc composites was the best. Compared with the pure MoS2 sensor, the responses of 7-CM to 1000 ppm formaldehyde (CH2O), acetone (C3H6O), ethanol (C2H6O), and 98% RH increased by 122.7, 734.6, 1639.8, and 440.5, respectively. The response of the heterojunction toward C2H6O was twice that of C3H6O and 13 times that of CH2O. In addition, the response time of all sensors was less than 60 s, and the recovery time was less than 10 s. These results provide an experimental reference for the development of high-performance MoS2-based gas sensors.