Low-Temperature Spark Plasma Sintering of ZrW2−xMoxO8 Exhibiting Controllable Negative Thermal Expansion

Molybdenum-doped zirconium tungstate (ZrW2−xMoxO8) has been widely studied because of its large isotropic coefficient of negative thermal expansion (NTE). However, low density and poor sinterability limit its production and application. In this study, relative density greater than 90% single-phase Z...

Full description

Saved in:
Bibliographic Details
Published inMaterials Vol. 11; no. 9; p. 1582
Main Authors Wei, Hui, Hasegawa, Marin, Mizutani, Shunsuke, Aimi, Akihisa, Fujimoto, Kenjiro, Nishio, Keishi
Format Journal Article
LanguageEnglish
Published Basel MDPI AG 01.09.2018
MDPI
Subjects
Online AccessGet full text

Cover

Loading…
More Information
Summary:Molybdenum-doped zirconium tungstate (ZrW2−xMoxO8) has been widely studied because of its large isotropic coefficient of negative thermal expansion (NTE). However, low density and poor sinterability limit its production and application. In this study, relative density greater than 90% single-phase ZrW2−xMoxO8 (0.0 ≤ x ≤ 1.0) sintered bodies were fabricated by spark plasma sintering (500–600 °C for 10 min) using ZrW2−xMoxO7(OH)2·2H2O precursor powders as the starting material. High-temperature X-ray diffraction and thermomechanical analysis were used to investigate the change in the order–disorder phase transition temperature of the sintered materials; it gradually dropped from 170 °C at x = 0.0 to 78 °C at x = 0.5, and then to below room temperature at x ≥ 0.7. In addition, all sintered bodies exhibited NTE behavior. The NTE coefficient was controllable by changing the x value as follows: from −7.85 × 10−6 °C−1 (x = 0) to −9.01 × 10−6 °C−1 (x = 0.6) and from −3.22 × 10−6 °C−1 (x = 0) to −2.50 × 10−6 °C−1 (x = 1.0) before and after the phase transition, respectively. Rietveld structure refinement results indicate that the change in the NTE coefficient can be straightforwardly traced to the thermodynamic instability of the terminal oxygen atoms, which only have one coordination.