Fabrication of superhydrophobic polymethylsilsesquioxane nanostructures on cotton textiles by a solution–immersion process

• Published in: Journal of colloid and interface science Vol. 359; no. 2; pp. 530 - 535
• Main Authors: Shirgholami, Mohammad A., Shateri Khalil-Abad, Mohammad, Khajavi, Ramin, Yazdanshenas, Mohammad E.
• Format: Journal Article
• Language: English
• Published: Amsterdam Elsevier Inc 15.07.2011; Elsevier
• Subjects: cellulose; Cellulose fibers; cellulosic fibers; Chemistry; Contact angle; Cotton; cotton fabric; Cotton textiles; energy-dispersive X-ray analysis; Exact sciences and technology; Fourier transform infrared spectroscopy; General and physical chemistry; hydrophobicity; industrial applications; Nanocomposites; Nanomaterials; Nanostructure; Nanostructures; reflectance; scanning electron microscopy; separation; Slippery; Solid-liquid interface; Sticky; Superhydrophobic; Surface physical chemistry; Textiles; Wettability; Cotton textiles; Superhydrophobic; Slippery; Nanostructures; Contact angle; Sticky; Water; Shape; Textile; Industrial application; Water repellent; Cellulose; Fiber; Immersion; Cotton; Precursor; Separation method; Wettability; Scanning electron microscopy; Nanostructure; Infrared spectrometry; Morphology; Phase separation; Fabric; Silane; Reflectance
• ISSN: 0021-9797; 1095-7103
• DOI: 10.1016/j.jcis.2011.04.031

SEM image (left) and 5 μL water droplet image (right) for polymethylsilsesquioxane nanofilaments-covered cotton fibers. [Display omitted] ► Superhydrophobic cotton fabrics by formation of polymethylsilsesquioxane nanostructures. ► Formation of polysiloxane nanostructures with different shapes and sizes. ► Tunable water-repellent properties of the fabric, from “sticky” to “slippery”. Superhydrophobic cotton textiles are prepared by a simple, one-step and inexpensive phase separation method under ambient conditions by which a layer of polymethylsilsesquioxane (PMSQ) nanostructures is covered onto the cellulose fibers. By changing the silane precursor concentration, PMSQ nanostructures with various shapes, morphologies and sizes were fabricated. Nanostructures were characterized using SEM, EDS, and attenuated total reflectance FTIR. The wettability of the modified cellulose surfaces was characterized with contact-angle goniometry and sliding angle technique, respectively. The water contact angle of modified cotton is measured to be higher than 150°, which is high enough to exhibit the lotus effect as a result of the superhydrophobicity. Tunable water-repellent properties of the fabric are also demonstrated, with sliding contact angles varying from “sticky” to “slippery” depending upon different nanostructures on the surface of the fibers. It is expected that this simple technique will accelerate the large-scale production of superhydrophobic cellulosic materials with new industrial applications.