Defect reconfiguration in a Ti–Al alloy via electroplasticity

It has been known for decades that the application of pulsed direct current can significantly enhance the formability of metals. However, the detailed mechanisms of this effect have been difficult to separate from simple Joule heating. Here, we study the electroplastic deformation of Ti–Al (7 at.% A...

Full description

Saved in:
Bibliographic Details
Published inNature materials Vol. 20; no. 4; pp. 468 - 472
Main Authors Zhao, Shiteng, Zhang, Ruopeng, Chong, Yan, Li, Xiaoqing, Abu-Odeh, Anas, Rothchild, Eric, Chrzan, Daryl C., Asta, Mark, Morris, J. W., Minor, Andrew M.
Format Journal Article
LanguageEnglish
Published London Nature Publishing Group UK 01.04.2021
Nature Publishing Group
Subjects
Online AccessGet full text

Cover

Loading…
More Information
Summary:It has been known for decades that the application of pulsed direct current can significantly enhance the formability of metals. However, the detailed mechanisms of this effect have been difficult to separate from simple Joule heating. Here, we study the electroplastic deformation of Ti–Al (7 at.% Al), an alloy that is uniquely suited for uncoupling this behaviour because, contrary to most metals, it has inherently lower ductility at higher temperature. We find that during mechanical deformation, electropulsing enhances cross-slip, producing a wavy dislocation morphology, and enhances twinning, which is similar to what occurs during cryogenic deformation. As a consequence, dislocations are prevented from localizing into planar slip bands that would lead to the early failure of the alloy under tension. Our results demonstrate that this macroscopic electroplastic behaviour originates from defect-level microstructural reconfiguration that cannot be rationalized by simple Joule heating. Transmission electron microscopy reveals the electroplastic effects in a Ti–Al alloy, which can be uncoupled from Joule heating effects. Electropulsing during deformation enhances wavy slip of dislocations, reconfiguring the dislocation pattern, and hence increases the ductility.
Bibliography:ObjectType-Article-1
SourceType-Scholarly Journals-1
ObjectType-Feature-2
content type line 14
content type line 23
ISSN:1476-1122
1476-4660
1476-4660
DOI:10.1038/s41563-020-00817-z