Effect of two different finishing systems on surface roughness of feldspathic and fluorapatite porcelains in ceramo-metal restorations: Comparative in vitro study

• Published in: Journal of International Society of Preventive & Community Dentistry Vol. 4; no. 1; pp. 22 - 28
• Main Authors: Anmol, Cherry, Soni, Sumeet
• Format: Journal Article
• Language: English
• Published: India Medknow Publications & Media Pvt. Ltd 01.01.2014; Medknow Publications & Media Pvt Ltd
• Subjects: Original; fluorapatite; Ceramo metal restoration; feldspathic; surface roughness
• ISSN: 2231-0762; 2250-1002
• DOI: 10.4103/2231-0762.127211

The objective of present study was to qualitatively and quantitatively evaluate and compare the effect of two ceramic finishing systems and diamond polishing paste on surface texture of two ceramic materials. The 40 test specimens were randomly divided into two main groups (Group I and Group II). Which were subsequently veneered with feldspathic porcelain and fluorapatite leucite porcelain systems respectively. The samples in Test group I and Test group II were subjected to different abrasion and finishing systems (Soft Lex and White silicon and grey rubber respectively). The surface roughness of all the four groups was assessed qualitatively using the scanning Electron Microscope and profilometer. The surface roughness of Feldspathic and fluorapetite porcelain increased after abrasion and finishing as compared to auto-glazed porcelin. The surface roughness was more in grey rubber disc group (Gp Ib) as compared to the soft lex disc groups. After polishing with the diamond paste, there was reduction in the surface roughness of both the disc groups. The Mean Ra values of the Feldspathic porcelain at three intervals were 0.52 ± 0.06, 0.54 ± 0.06, 0.32 ± 0.06 and 0.50 ± 0.04, 1.25 ± 0.10, 0.45 ± 0.6 respectively for grey rubber disc and soft lex groups. The Mean Ra values of Fluorapetite porcelain at three intervals were 0.40 ± 0.06, 0.52 ± 0.06, 0.30 ± 0.03 and 0.41 ± 0.04, 1.17 ± 0.09, 0.39 ± 0.07 respectively for grey rubber disc and soft lex groups. The surface roughness was less in the polished samples as compared to the auto-glazed porcelain. The findings were more reinforcing in the soft lex group as compared to the white/grey rubber disc group. Between the two porcelain systems, the Fluorapatite leucite porcelain specimens exhibited better surface smoothness than feldspathic porcelain.