Low elastic modulus Ti–Ta alloys for load-bearing permanent implants: Enhancing the biodegradation resistance by electrochemical surface engineering

• Published in: Materials Science & Engineering C Vol. 46; pp. 226 - 231
• Main Authors: Kesteven, Jazmin, Kannan, M. Bobby, Walter, Rhys, Khakbaz, Hadis, Choe, Han-Choel
• Format: Journal Article
• Language: English
• Published: Netherlands Elsevier B.V 01.01.2015
• Subjects: Alloys; Anodization; Biocompatible Materials; Biomaterials; Bones; Calcium phosphate; Coating; Degradation; Elastic modulus; Electrochemical Techniques - methods; Microscopy, Electron, Scanning; Modulus of elasticity; Prostheses and Implants; Surface Properties; Surgical implants; Tantalum; Tantalum - chemistry; Titanium; Titanium - chemistry; Titanium base alloys; Degradation; Titanium; Calcium phosphate; Tantalum; Anodization; Biomaterials
• ISSN: 0928-4931; 1873-0191
• DOI: 10.1016/j.msec.2014.10.038

In this study, the in vitro degradation behaviour of titanium–tantalum (Ti–Ta) alloys (10–30wt.% Ta) was investigated and compared with conventional implant materials, i.e., commercially pure titanium (Cp-Ti) and titanium–aluminium–vanadium (Ti6Al4V) alloy. Among the three Ti–Ta alloys studied, the Ti20Ta (6.3×10−4mm/y) exhibited the lowest degradation rate, followed by Ti30Ta (1.2×10−3mm/y) and Ti10Ta (1.4×10−3mm/y). All the Ti–Ta alloys exhibited lower degradation rate than that of Cp-Ti (1.8×10−3mm/y), which suggests that Ta addition to Ti is beneficial. As compared to Ti6Al4V alloy (8.1×10−4mm/y), the degradation rate of Ti20Ta alloy was lower by ~22%. However, the Ti30Ta alloy, which has closer elastic modulus to that of natural bone, showed ~48% higher degradation rate than that of Ti6Al4V alloy. Hence, to improve the degradation performance of Ti30Ta alloy, an intermediate thin porous layer was formed electrochemically on the alloy followed by calcium phosphate (CaP) electrodeposition. The coated Ti30Ta alloy (3.8×10−3mm/y) showed ~53% lower degradation rate than that of Ti6Al4V alloy. Thus, the study suggests that CaP coated Ti30Ta alloy can be a viable material for load-bearing permanent implants. •In vitro degradation of titanium–tantalum (Ti–Ta) alloys was studied.•Ta addition to Ti is beneficial for better degradation resistance.•Ti–Ta alloys perform better than commercially pure Ti.•Calcium phosphate coated Ti–Ta alloy is superior to Ti6Al4V alloy.