Hot deformation behavior of Mg-Zn-Al alloy tube processed by severe plastic deformation
In the current study, severe plastic deformation (SPD) was applied on a commercial Mg-3Al-1Zn alloy tubes via parallel tubular channel angular pressing (PTCAP) route. Different passes of PTCAP process were applied, and microstructure, hardness and tensile properties at the room, and elevated tempera...
Saved in:
Published in | Archives of metallurgy and materials Vol. 62; no. 1; pp. 159 - 166 |
---|---|
Main Authors | , , , |
Format | Journal Article |
Language | English |
Published |
Warsaw
De Gruyter Open
01.03.2017
Polish Academy of Sciences |
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | In the current study, severe plastic deformation (SPD) was applied on a commercial Mg-3Al-1Zn alloy tubes via parallel tubular channel angular pressing (PTCAP) route. Different passes of PTCAP process were applied, and microstructure, hardness and tensile properties at the room, and elevated temperatures were evaluated. The results showed that bimodal microstructure appeared and led to AZ31 alloy represented higher hardness, higher strength with a reasonable elongation at room temperature. Similarly, very high elongation to failure was achieved at a higher temperature. The increase in the number of SPD passes up to two, leads to increasing the ductility up to 263% at 400°C. Then, an increase in the number of PTCAP passes to three, leads to decrease in the ductility as the results of formation of microvoids when SPD processing at higher equivalent strains without a sufficient hydrostatic compressive stress. Relatively ductile fracture mode was also occurred in all samples. |
---|---|
ISSN: | 2300-1909 1733-3490 2300-1909 |
DOI: | 10.1515/amm-2017-0022 |