Impact-induced bonding process of copper at low velocity and room temperature
[Display omitted] •A novel impact-induced bonding process at low velocity and room temperature is proposed for revealing bonding mechanisms•The embedding between microstructures and the recrystallization of grains are significant bonding mechanisms•The maximum bonding strength of the bonding interfa...
Saved in:
Published in | Materials & design Vol. 226; p. 111603 |
---|---|
Main Authors | , , , , , , , , |
Format | Journal Article |
Language | English |
Published |
Elsevier Ltd
01.02.2023
Elsevier |
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | [Display omitted]
•A novel impact-induced bonding process at low velocity and room temperature is proposed for revealing bonding mechanisms•The embedding between microstructures and the recrystallization of grains are significant bonding mechanisms•The maximum bonding strength of the bonding interface can exceed 95% of the strength of bulk material
The impact-induced bonding can be foundation of fast solid-state additive manufacturing. The mechanisms behind impact-induced bonding have not been widely acknowledged due to complexity caused by too transient process and extreme loading conditions. We report a novel impact-induced bonding process of copper flakes. This bonding process possesses attractive features of longer duration, macroscopic characteristic length and low ambient temperature (typically at room temperature). Meanwhile, finite element simulation based on actual grain configurations and crystal plasticity reveals that the bonding strength can reach the strength of bulk material. Three types of bonding modes are observed and corresponding mechanisms are extracted. It is found that the embedding between microstructures and the recrystallization of grains are significant factors of impact-induced bonding. Both microstructure characterization and simulation with material point method support recrystallization but not melting. |
---|---|