Controlling grain size and texture in Mg–Zn–Mn alloys from the interaction of recrystallization and precipitation

The recrystallization behavior of extruded Mg–Zn–Mn alloys was systematically investigated under different aging treatment prior to extrusion. Electron backscattered diffraction analysis was used to explore the recrystallization mechanism and corresponding effects on the basal texture of alloys duri...

Full description

Saved in:
Bibliographic Details
Published inJournal of materials research and technology Vol. 21; pp. 1395 - 1407
Main Authors Wu, Xiong, Jing, Xuerui, Xiao, Hui, Ouyang, Sihui, Tang, Aitao, Peng, Peng, Feng, Bo, Rashad, Muhammad, She, Jia, Chen, Xianhua, Zheng, Kaihong, Pan, Fusheng
Format Journal Article
LanguageEnglish
Published Elsevier B.V 01.11.2022
Elsevier
Subjects
Heat treatment
Magnesium alloys
Mechanical property
Recrystallization
Heat treatment
Magnesium alloys
Mechanical property
Recrystallization
Online AccessGet full text

Cover

More Information
Summary:The recrystallization behavior of extruded Mg–Zn–Mn alloys was systematically investigated under different aging treatment prior to extrusion. Electron backscattered diffraction analysis was used to explore the recrystallization mechanism and corresponding effects on the basal texture of alloys during extrusion. The results show that the primary coarse particles can effectively promote recrystallization nucleation. Moreover, the precipitation of nanoscale particles during the aging process play a role in pinning the grain boundaries. Therefore, after peak-aged treatment (16 h), the extruded Mg alloy obtains uniform and fine microstructure, showing good mechanical properties: the tensile yield strength, tensile strength, elongation, compressive yield strength, and tension-compression yield asymmetry were 298 MPa, 363 MPa, 26%, 260 MPa, and 0.87, respectively.
ISSN:2238-7854
DOI:10.1016/j.jmrt.2022.09.108