Investigation on Fatigue Threshold Testing Methods in a Near Lamellar TiAl Alloy

• Published in: Materials Vol. 12; no. 21; p. 3487
• Main Authors: Wang, Shiyuan, Li, Hangyue, Bowen, Paul
• Format: Journal Article
• Language: English
• Published: Basel MDPI AG 24.10.2019; MDPI
• Subjects: Alloys; Crack initiation; Crack propagation; fatigue crack growth; fatigue crack threshold; Fatigue failure; fatigue testing method; Fatigue tests; Fracture mechanics; Intermetallic compounds; Lamellar structure; Load shedding; load-increasing method; Machining; Metal fatigue; Methods; Morphology; near lamellar γ-tial alloy; Precracking; Room temperature; Starters; Test procedures; Titanium aluminides; Titanium base alloys
• ISSN: 1996-1944; 1996-1944
• DOI: 10.3390/ma12213487

The effects of influential fatigue testing factors, including loading schemes (e.g., traditional load shedding and staircase load increasing), morphology of crack starters, and precracking approaches on the near-threshold fatigue crack growth behaviors for a near lamellar γ-TiAl alloy (Ti-45Al-2Mn-2Nb-1B) were investigated at room temperature and 650 °C. The results showed that the measured fatigue threshold values in lamellar γ-TiAl alloys are very sensitive to the applied testing procedures. For example, the staircase load-increasing method yielded smaller threshold values. When such a load-increasing method was used, the threshold values were measured either from a notch machined by electro-discharge machining or prepared by a compression–compression fatigue loading. Moreover, some differences could be seen with respect to the morphologies of the crack starters. Most of the above influences are associated with the brittle nature of the material and the characteristics of the lamellar microstructures, and closure effects are primarily induced by crack wake roughness or unbroken ligaments.