Cleaning of diffusion bonding surface by argon ion bombardment treatment

• Published in: Nuclear instruments & methods in physics research. Section B, Beam interactions with materials and atoms Vol. 206; no. Complete; pp. 219 - 223
• Main Authors: Wang, Airu, Ohashi, Osamu, Yamaguchi, Norio, Aoki, Masanori, Higashi, Yasuo, Hitomi, Nobuteru
• Format: Journal Article
• Language: English
• Published: Elsevier B.V 01.05.2003
• Subjects: Argon ion bombardment; Atomic force microscopy; Diffusion bonding; Fracture surface; Inclusion; 68.35.FX; Argon ion bombardment; Atomic force microscopy; Inclusion; 68.35.−P; 61.20.−X; Fracture surface; Diffusion bonding; 61.72.Qq
• ISSN: 0168-583X; 1872-9584
• DOI: 10.1016/S0168-583X(03)00732-8

The specimens of oxygen-free high conductivity copper, SUS304L stainless steel and pure iron were treated by argon ion bombardment and then were bonded by diffusion bonding method. The effects of argon ion bombardment treatment on faying surface morphology, tensile strength of bonding joints and inclusions at the fracture surface were investigated. The results showed that argon ion bombardment treatment was effective to remove the oxide film and contamination at the faying surface and improve the quality of joints. The tensile strength of the bonded joints was improved, and minimum bonding temperature to make the metallic bonding at the interface was lowered by argon ion bombardment treatment. At the joints with argon ion bombardment treatment, ductile fractured surface was seen and the amount of inclusions was obviously decreased.