Comparative Study on the Corro-Erosive Properties of Base Cemented Transition Metals TaC and HfC and TaX-HfX-C Coatings

• Published in: Metals (Basel ) Vol. 12; no. 9; p. 1516
• Main Authors: Ortiz, C. H., Sanchez, S. S., Caicedo, J. C., Aperador, W., Sánchez-Molina, Jorge, Ruiz, J. Bautista
• Format: Journal Article
• Language: English
• Published: Basel MDPI AG 01.09.2022
• Subjects: Ablation; abrasive particles; Carbon; Coatings; Comparative analysis; Comparative studies; corro-erosive study; Corrosion potential; Corrosion rate; Corrosion resistance; electrochemical properties; Electrodes; Flow velocity; Hafnium carbide; Hydrofluorocarbons; Phase transitions; Protective coatings; Silicon; Structural damage; Taxation; Transition metals; wear; United States > US; Massachusetts
• ISSN: 2075-4701; 2075-4701
• DOI: 10.3390/met12091516

In this research, we report on a comparative study of the corro-erosive properties of TaC and HfC individual coatings and (Ta70-Hf30-C) and (Ta30-Hf70-C) coatings. These were subjected to different impact angles of abrasive particles, corresponding with angles of 30°, 60° and 90°. It was determined that at 90°, a higher structural damage of the coatings obtained was presented. In addition, for all the systems, it was possible to conclude that the coating formed by (Ta30-Hf70-C) presented a roughness of approximately 7.11 nm, which influenced corrosive properties such as the corrosion potential and corrosion rate. Finally, it was possible to conclude that the (Ta30-Hf70-C) coating presented a higher resistance against corro-erosive environments. This was attributed to structural and mainly superficial factors, making this coating the best option to be implemented as a protective coating against highly aggressive environments in industry.