Stress intensity factors for axial semi-elliptical surface cracks and embedded elliptical cracks at longitudinal butt welded joints of steel-lined pressure tunnels and shafts considering weld shape

• Published in: Engineering fracture mechanics Vol. 179; pp. 93 - 119
• Main Authors: Pachoud, A.J., Manso, P.A., Schleiss, A.J.
• Format: Journal Article
• Language: English
• Published: New York Elsevier Ltd 15.06.2017; Elsevier BV
• Subjects: Axial stress; Butt joints; Butt welding; Crack propagation; Cracking (fracturing); Cracks; Embedded cracks; Fatigue cracking; Fatigue cracks; Fatigue failure; Finite element analysis; Finite element method; Fracture mechanics; High strength steels; Parametric equations; Pressure tunnels; Rock (material); Steel liners; Stress intensity; Stress intensity factors; Surface cracks; Tunnel linings; Weld defects; Welded joints; Embedded cracks; Stress intensity factors; Finite element analysis; Steel liners; Surface cracks
• ISSN: 0013-7944; 1873-7315
• DOI: 10.1016/j.engfracmech.2017.04.024

•SIF of axial cracks in the weld material of steel liners were studied by means of FEA.•Peaking at the longitudinal butt welded joint is considered.•The weld profile is modeled with splines and the FE model is built parametrically.•Semi-elliptical surface cracks and embedded elliptical cracks are studied.•A new parametric weld shape correction factor is proposed for semi-elliptical surface cracks. When for steel liners of pressure tunnels and shafts high-strength steels are used, welded joints are subject to the risk of hydrogen induced cold-cracking in the base material. Longitudinal butt welded joints are critical regions as they are loaded transversely. For an accurate engineering fatigue and fracture assessment, solutions for stress intensity factors (SIF) are required, considering the weld shape and the global behavior of the liner (i.e., geometrical imperfections and interaction with surrounding concrete and rock). In this study, SIF for axial semi-elliptical surface cracks and embedded elliptical cracks at longitudinal butt welded joints of steel liners are studied by means of the finite element method. At first the applicability of published parametric equations for SIF of elliptical cracks in plates is validated. Then the influence of the weld shape is assessed through a systematic parametric study. It is shown that the weld profile has a significant influence on SIF for semi-elliptical surface cracks while it has no significant influence on SIF for embedded elliptical cracks within the studied range of relative crack depth. Finally, a new parametric equation is proposed to estimate the weld shape correction factor for semi-elliptical surface cracks.