Texture and microstructure at the surface of an AISI D2 steel treated by high current pulsed electron beam

Surface modifications were investigated for an AISI D2 steel after 25 pulses of high current pulsed electron beam (HCPEB) treatment. In particular, X-ray diffraction (XRD) was used to determine the thickness, nature of phase, and texture in the top surface melted layer. The mechanisms responsible fo...

Full description

Saved in:
Bibliographic Details
Published inMetallurgical and materials transactions. A, Physical metallurgy and materials science Vol. 38; no. 9; pp. 2061 - 2071
Main Authors ZOU, J. X, GROSDIDIER, T, BOLLE, B, ZHANG, K. M, DONG, C
Format Journal Article
LanguageEnglish
Published New York, NY Springer 01.09.2007
Springer Nature B.V
Subjects
Online AccessGet full text

Cover

Loading…
More Information
Summary:Surface modifications were investigated for an AISI D2 steel after 25 pulses of high current pulsed electron beam (HCPEB) treatment. In particular, X-ray diffraction (XRD) was used to determine the thickness, nature of phase, and texture in the top surface melted layer. The mechanisms responsible for the structure and texture evolutions were further asserted by scanning electron microscopy (SEM) and electron backscattering diffraction (EBSD) results. Under the action of the beam, the large carbides present in the steel were melted and dissolved so that the top surface rapidly solidified as a 3-µm-thick layer of ultra-fine-grained metastable austenite without any martensite formation. The growth of the γ phase led to an unusual + fiber solidification texture. In addition, Σ3-twin boundaries were observed to bridge, most often, near domains. These features, observed here in a Fe supersaturated and highly undercooled melt, are discussed in light of recent findings on atypical growth in directionally solidified Al-based alloys.[40-42] Comparatively, the α phase present in the heat-affected zone remained randomly oriented. [PUBLICATION ABSTRACT]
Bibliography:ObjectType-Article-2
SourceType-Scholarly Journals-1
ObjectType-Feature-1
content type line 23
ISSN:1073-5623
1543-1940
DOI:10.1007/s11661-007-9146-1