Experimental Study of Post Installed Rebar Anchor Systems for Concrete Structure

• Published in: Civil and environmental engineering (Berlin) Vol. 16; no. 2; pp. 308 - 319
• Main Authors: Haidar, Haidar H., Mussa, Faten I., Dawood, Abbas O., Ghazi, Ahmed A., Gabbar, Rassel A.
• Format: Journal Article
• Language: English
• Published: Sciendo 01.12.2020
• Subjects: Adhesive bonded anchor; Failure mode; Kut epoxy anchor; Pull-out test; SIKAFLOOR
• ISSN: 1336-5835; 2199-6512
• DOI: 10.2478/cee-2020-0031

This study investigated the effectiveness of several types of adhesives used in post-installed rebar connections as a bonding agent between steel reinforcement bars and old concrete under pull out test. The experimental samples were; cylindrical samples of (150 mm dia. × 300 mm high) with anchors rebar of varying diameter (12 and 16 mm), different embedded length (100 and 150) mm with different holes’ diameters. The strategy of control were cast-in-place rebar concrete specimens while other samples are post-installed rebar concrete specimens of varied chemical adhesives as bonding agents, namely KUT EPOXY ANCHOR ‘NS’ and SIKAFLOOR169. The output showed that the different adhesives yielded closed pull-out load values. It is found that the pull-out capacity (bond strength) is increased by increasing the embedded length, the diameter of the rebar and slightly with the diameter of the hole. In addition, the failure mode of post-installed rebar concrete was governed by the embedded length and the area of contact with the adhesives. On the other hand, the larger diameter of rebar favors splitting or failure of concrete due to higher strength in binder-rebar interface compare to the binder-concrete interface. The results showed that the pull-out load was increased by (26 % and 32 %) as the rebar diameter increased from 12 mm to 16 mm for KUT “NS” and SIKAFLOOR respectively. The hole diameter had slightly effect of the pull out load where the average of increment was only 6 %. Finally, the bonding strength is considerably depended on the embedded length and less affected by the type of epoxy.