Production of dense ceramics based on magnesium aluminate spinel with an evaporating additive
The influence of the evaporating additive on the properties of ceramics based on magnesium aluminate spinel obtained by high-temperature sintering in vacuum was investigated. The spinel precursor was obtained by chemical reverse co-precipitation, which after that was calcined at a temperature of 120...
Saved in:
Published in | IOP conference series. Materials Science and Engineering Vol. 971; no. 3; pp. 32008 - 32013 |
---|---|
Main Authors | , , |
Format | Journal Article |
Language | English |
Published |
Bristol
IOP Publishing
01.11.2020
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | The influence of the evaporating additive on the properties of ceramics based on magnesium aluminate spinel obtained by high-temperature sintering in vacuum was investigated. The spinel precursor was obtained by chemical reverse co-precipitation, which after that was calcined at a temperature of 1200 °C. As an additive, boron oxide B2O3 was used in the concentration range of 5.0-7.0 wt.% Sintering of the samples was carried out at temperatures of 1700 and 1750 °C. Identified trends allowing to obtain the densest samples with minimal porosity. |
---|---|
ISSN: | 1757-8981 1757-899X |
DOI: | 10.1088/1757-899X/971/3/032008 |