High Rate Characterization of Three DP980 Steels

• Published in: EPJ Web of Conferences Vol. 183; p. 2060
• Main Authors: Zhumagulov, Amir, Abedini, Armin, Rahmaann, Taamjeed, Imbert, José, Butcher, Clifford, Worswick, Michael, Malcolm, Skye, Dykeman, Jim, Ezzat, Hesham
• Format: Journal Article Conference Proceeding
• Language: English
• Published: Les Ulis EDP Sciences 01.01.2018
• Subjects: Automobile industry; Automotive engineering; Automotive parts; Elongation; Energy absorption; Fuel consumption; High strength steels; Iron and steel making; Modelling; Sensitivity; Shear tests; Static tests; Weight reduction; Yield point
• ISSN: 2100-014X; 2101-6275; 2100-014X
• DOI: 10.1051/epjconf/201818302060

Advanced high strength steels (AHSS) are used extensively in the automotive industry in the ongoing effort to reduce vehicle weight. Their increased strength allows for the reduction of sheet thickness, and thus a reduction in mass, while offering formability and cost advantages when compared to other metal alloys typically considered for lightweight applications. DP980 steels are AHSS being considered for structural energy absorbing components; however, there is a lack of published information on their high rate behaviour. This paper presents the results of an experimental program that characterized three production DP980 steels from three different manufacturers at strain rates of 0.001, 1, 10, 100 and 1,000 s -1 . An electro-mechanical frame was used for the quasi-static tests, the 1, 10, and 100 s -1 tests were carried out using a fast hydraulic apparatus and the 1,000 s -1 experiments were carried out using a tensile split Hopkinson bar. The quasi-static hardening response at strains higher than the uniform elongation of about 7% was obtained by using a shear test, thus avoiding the use of inverse modelling techniques. The results indicate that the DP980 steels are moderately rate sensitive, with one of the materials showing higher sensitivity than the others. One of the materials exhibited a yield point phenomenon that appears to affect the behaviour of the material at 100 and 1,000 s -1 , however, the reasons for this behaviour remain an open question. The data was fit to modified Johnson-Cook and Cowper-Symonds model to account for rate sensitivity. The results presented in this paper provide a tool for modelling the dynamic behaviour of DP980 steels.