Assessment of Changes in Abrasive Wear Resistance of a Welded Joint of Low-Alloy Martensitic Steel Using Microabrasion Test

• Published in: Materials Vol. 17; no. 9; p. 2101
• Main Authors: Ligier, Krzysztof, Napiórkowski, Jerzy, Lemecha, Magdalena
• Format: Journal Article
• Language: English
• Published: Switzerland MDPI AG 01.05.2024
• Subjects: Abrasion resistance; Abrasion resistant alloys; Abrasion resistant steels; Abrasive wear; Alloys; Analysis; Arc welding machines; Cratering; Friction; Heat resistant steels; High temperature; Low alloy steels; Manufacturers; Martensitic stainless steels; Mechanical properties; Methods; Specialty metals industry; Steel; Tribology; Wear rate; Wear resistance; Welded joints; Welding; Poland; abrasive wear; ball-cratering method; wear testing; welded joint
• ISSN: 1996-1944; 1996-1944
• DOI: 10.3390/ma17092101

Martensitic low-alloy steels are widely used in machine construction. Due to their declared weldability, arc welding is most often used to join elements made of this type of steel. However, the high temperature associated with welding causes unfavourable changes in the microstructure, resulting in reduced abrasion resistance. Therefore, it is important to know the tribological properties of the welded joint. This article presents the results of a study on the abrasion wear resistance of a welded joint of an abrasion-resistant steel. This study tested a welded joint of an abrasive-resistant steel produced by the arc welding method. Wear testing of the welded joint was carried out under laboratory conditions by the ball-cratering method in the presence of abrasive slurry on the cross-section of the welded joint. Based on the test results, the change in the abrasive wear rate of the material as a function of the distance from the welded joint axis was determined. It was also found that the thermal processes accompanying welding caused structural changes that increased the wear rate index value. Adverse changes in the tribological properties of a welded material persist up to a distance of approx. 20 mm from the weld centre.