Experimental Phase Diagram of the Al–Mo–Gd Ternary System at 773 K
The nature of the isothermal region of the Al–Mo–Gd ternary system at 773 K has been established by analysis of quenched samples, annealed for 6 weeks, by use of x-ray powder diffraction and scanning electron microscopy equipped with energy-dispersive analysis. Two ternary phases, Al 43 Mo 4 Gd 6 an...
Saved in:
Published in | Journal of phase equilibria and diffusion Vol. 36; no. 3; pp. 218 - 223 |
---|---|
Main Authors | , , , , , , , |
Format | Journal Article |
Language | English |
Published |
New York
Springer US
01.06.2015
Springer Nature B.V |
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | The nature of the isothermal region of the Al–Mo–Gd ternary system at 773 K has been established by analysis of quenched samples, annealed for 6 weeks, by use of x-ray powder diffraction and scanning electron microscopy equipped with energy-dispersive analysis. Two ternary phases, Al
43
Mo
4
Gd
6
and Al
4
Mo
2
Gd were observed. Ten binary phases, including Al
17
Mo
4
rather than Al
4
Mo, were present at 773 K in the Al–Mo system. The ranges of homogeneity of the AlMo
3
and Al
8
Mo
3
phases were 7.5 and 1 at.%, respectively. According to results obtained from the disappearing-phase method, the maximum solubility of Al in Mo is approximately 16 at.%. |
---|---|