Effect of hot humid environmental exposure on fatigue crack growth of adhesive-bonded aluminum A356 joints
In this study, the effect of hot humid environmental exposure prior to and after adhesive curing on the fatigue crack growth (FCG) behavior of adhesive-bonded aluminum A356 joints was investigated by using single-edge notch bend (SENB) specimen. The results showed that while the exposure after adhes...
Saved in:
Published in | International journal of adhesion and adhesives Vol. 40; pp. 1 - 10 |
---|---|
Main Authors | , , , |
Format | Journal Article |
Language | English |
Published |
Kidlington
Elsevier Ltd
01.01.2013
Elsevier |
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | In this study, the effect of hot humid environmental exposure prior to and after adhesive curing on the fatigue crack growth (FCG) behavior of adhesive-bonded aluminum A356 joints was investigated by using single-edge notch bend (SENB) specimen. The results showed that while the exposure after adhesive curing had a significant effect on the FCG resistance of the joints, the exposure of the assembled joints prior to adhesive curing had a relatively small influence. In addition, the effect of load ratio R on the FCG behavior of the exposed joints was studied. The results showed that the FCG of the exposed joints is more sensitive to load ratio R than that of the unexposed joints. |
---|---|
ISSN: | 0143-7496 1879-0127 |
DOI: | 10.1016/j.ijadhadh.2012.08.008 |