Leaching kinetics of zinc silicate in ammonium chloride solution
The leaching kinetics of zinc silicate in ammonium chloride solution was investigated. The effects of stirring speed (150–400 r/min), leaching temperature (95–108 °C), particle size of zinc silicate (61–150 μm) and the concentration of ammonium chloride (3.5–5.5 mol/L) on leaching rate of zinc were...
Saved in:
Published in | Transactions of Nonferrous Metals Society of China Vol. 26; no. 6; pp. 1688 - 1695 |
---|---|
Main Authors | , , , , , |
Format | Journal Article |
Language | English |
Published |
Elsevier Ltd
01.06.2016
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | The leaching kinetics of zinc silicate in ammonium chloride solution was investigated. The effects of stirring speed (150–400 r/min), leaching temperature (95–108 °C), particle size of zinc silicate (61–150 μm) and the concentration of ammonium chloride (3.5–5.5 mol/L) on leaching rate of zinc were studied. The results show that decreasing the particle size of zinc silicate and increasing the leaching temperature and concentration of ammonium chloride can obviously enhance the leaching rate of zinc. Among the kinetic models of the porous solids tested, the grain model with porous diffusion control can well describe the zinc leaching kinetics. The apparent activation energy of the leaching reaction is 161.26 kJ/mol and the reaction order with respect to ammonium chloride is 3.5. |
---|---|
Bibliography: | ObjectType-Article-1 SourceType-Scholarly Journals-1 ObjectType-Feature-2 content type line 23 |
ISSN: | 1003-6326 |
DOI: | 10.1016/S1003-6326(16)64278-4 |