Rheo-optical two-dimensional (2D) near-infrared (NIR) correlation spectroscopy for probing strain-induced molecular chain deformation of annealed and quenched Nylon 6 films

• Published in: Journal of molecular structure Vol. 1158; pp. 271 - 276
• Main Authors: Shinzawa, Hideyuki, Mizukado, Junji
• Format: Journal Article
• Language: English
• Published: Elsevier B.V 15.04.2018
• Subjects: Near-infrared (NIR); Nylon 6; Rheo-optical spectroscopy; Tensile test; Two-dimensional (2D) correlation spectroscopy; Nylon 6; Rheo-optical spectroscopy; Two-dimensional (2D) correlation spectroscopy; Tensile test; Near-infrared (NIR)
• ISSN: 0022-2860; 1872-8014
• DOI: 10.1016/j.molstruc.2018.01.025

A rheo-optical characterization technique based on the combination of a near-infrared (NIR) spectrometer and a tensile testing machine is presented here. In the rheo-optical NIR spectroscopy, tensile deformations are applied to polymers to induce displacement of ordered or disordered molecular chains. The molecular-level variation of the sample occurring on short time scales is readily captured as a form of strain-dependent NIR spectra by taking an advantage of an acousto-optic tunable filter (AOTF) equipped with the NIR spectrometer. In addition, the utilization of NIR with much less intense absorption makes it possible to measure transmittance spectra of relatively thick samples which are often required for conventional tensile testing. An illustrative example of the rheo-optical technique is given with annealed and quenched Nylon 6 samples to show how this technique can be utilized to derive more penetrating insight even from the seemingly simple polymers. The analysis of the sets of strain-dependent NIR spectra suggests the presence of polymer structures undergoing different variations during the tensile elongation. For instance, the tensile deformation of the semi-crystalline Nylon 6 involves a separate step of elongation of the rubbery amorphous chains and subsequent disintegration of the rigid crystalline structure. Excess amount of crystalline phase in Nylon 6, however, results in the retardation of the elastic deformation mainly achieved by the amorphous structure, which eventually leads to the simultaneous orientation of both amorphous and crystalline structures. [Display omitted] •Rheo-optical NIR technique is applied to Nylon 6 samples.•Quenched and annealed samples showed different spectral features when subjected to deformation.•Excess amount of crystalline structure essential restricts the orientation of amorphous, making the sample hard and brittle.