The effect of microarc oxidation and excimer laser processing on the microstructure and corrosion resistance of Zr–1Nb alloy

• Published in: Journal of nuclear materials Vol. 467; no. Part 1; pp. 186 - 193
• Main Authors: Yang, Jiaoxi, Wang, Xin, Wen, Qiang, Wang, Xibing, Wang, Rongshan, Zhang, Yanwei, Xue, Wenbin
• Format: Journal Article
• Language: English
• Published: Elsevier B.V 01.12.2015
• Subjects: Cladding; Corrosion resistance; Excimer lasers; High temperature corrosion; MAO + laser treatment; Oxidation; Pre-oxide film; Rietveld analysis; Thermal expansion; Tubes; Zirconium; Zirconium base alloys; Zr-1Nb cladding tube; MAO + laser treatment; Pre-oxide film; Rietveld analysis; Zr-1Nb cladding tube; High temperature corrosion
• ISSN: 0022-3115; 1873-4820
• DOI: 10.1016/j.jnucmat.2015.09.033

The main purpose of this research was to investigate the effect of microarc oxidation (MAO) and excimer laser processing on the corrosion resistance of Zr–1Nb alloy in service environment. The pre-oxide film was fabricated on the surface of Zr–1Nb cladding tubes by MAO processing, and then subjected to KrF excimer laser irradiation. The surface morphology of the pre-oxide film was observed using a scanning electron microscope; phase compositions and quantities were determined using an X-ray diffraction; surface roughness was determined using a profilometer; and thermal expansion coefficient was measured using a dilatometer. Autoclave experiments were conducted for 94 days in an aqueous condition of 360 °C under 18.6 MPa in 0.01 mol/L LiOH solutions. The results showed that MAO + laser treatment resulted in a significant increase in the corrosion resistance of Zr–1Nb cladding tubes at high temperatures, because laser melting and etching could lead to a reduction in surface roughness and an increase in compactness of the pre-oxide film, and laser processing could promote the transformation of m-ZrO2 phase to t-ZrO2 phase. The best corrosion resistance was obtained when the pulse energy was 500 mJ, scanning speed was 0.13 mm/s, and pulse number was 2400. •Pre-oxide film was fabricated on Zr–1Nb cladding tube by MAO+ excimer laser processing.•Excimer laser processing induced the transformation of m-ZrO2 to t-ZrO2.•The Rietveld quantitative analysis of the pre-oxide film was made.•We investigated the high temperature corrosion and corrosion mechanism of the oxide film.•The parameters of MAO+ excimer laser processing were optimized.