The fatigue parameters of welded joints made of FV520B were obtained considering the real operating situations. The fatigue fracture types were divided into two groups. The scanning electron microscope (SEM) was applied to carefully study the fatigue fracture surfaces so as to investigate the fatigu...
Saved in:
Published in | Applied Mechanics and Materials Vol. 121-126; pp. 559 - 563 |
---|---|
Main Authors | , , , , |
Format | Journal Article |
Language | English |
Published |
Zurich
Trans Tech Publications Ltd
01.01.2012
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | The fatigue parameters of welded joints made of FV520B were obtained considering the real operating situations. The fatigue fracture types were divided into two groups. The scanning electron microscope (SEM) was applied to carefully study the fatigue fracture surfaces so as to investigate the fatigue failure mechanisms. The microstructures of the base metal and the weld seam were studied by the metallographic microscope (MM), SEM and TEM in support of the dissimilar mechanical property analysis. The present paper concluded that the fatigue microcracks mainly initiated from the surface near the weld toe and inclusions in the weld seam, the heat-affected zone (HAZ) disappeared due to the postweld heat-treatment processes, and that the fatigue resistance of the base metal was better than the weld seam. |
---|---|
Bibliography: | Selected, peer reviewed papers from the Second International Conference on Frontiers of Manufacturing and Design Science, (ICFMD 2011), December 11-13, Taiwan |
ISBN: | 3037852828 9783037852828 |
ISSN: | 1660-9336 1662-7482 1662-7482 |
DOI: | 10.4028/www.scientific.net/AMM.121-126.559 |