Modelling of damage and failure of glass/epoxy composite plates subject to impact fatigue

• Published in: International journal of fatigue Vol. 23; no. 10; pp. 877 - 885
• Main Authors: Azouaoui, K, Rechak, S, Azari, Z, Benmedakhene, S, Laksimi, A, Pluvinage, G
• Format: Journal Article
• Language: English
• Published: Oxford Elsevier Ltd 01.11.2001; Elsevier Science
• Subjects: Applied sciences; Damage; Delamination; Exact sciences and technology; Forms of application and semi-finished materials; Glass/epoxy; Impact fatigue; Laminates; Photomicrography; Polymer industry, paints, wood; Technology of polymers; Glass/epoxy; Impact fatigue; Damage; Photomicrography; Delamination; Laminate; Fiber reinforced material; Mechanical properties; Epoxy resin; Experimental study; Modeling; Composite material; Plate; Impact strength; Fatigue strength; Glass fiber; Comparative study; Fracture mode; Damaging
• ISSN: 0142-1123; 1879-3452
• DOI: 10.1016/S0142-1123(01)00050-0

An investigation has been carried out to study the impact fatigue damage of glass/epoxy laminated composites. Accumulation of damage, such as matrix cracking, delamination and fibre breakage, with repeated impact of the composite material may reduce the overall stiffness. These damage modes have been combined in a very complicated way to describe damage growth and fracture. A model is proposed for characterising the damage as a function of the normalised impact number. The scalar variable D, which characterises the material damage, is written as a function of the life duration β, using a modified form of the Mankowsky empirical law [Int J Solids Struct 32(11) (1995) 1607]. The macroscopic failure mode and the internal damage in laminated specimens of glass/epoxy as a consequence of impact fatigue are analysed at different levels of incident impact energy. The impact fatigue tests have been conducted on an apparatus built in our laboratory.