Cavity Behavior of Fine-Grained 5A70 Aluminum Alloy during Superplastic Formation

• Published in: Metals (Basel ) Vol. 8; no. 12; p. 1065
• Main Authors: Li, Sheng, Jin, Shunyao, Huang, Zhongguo
• Format: Journal Article
• Language: English
• Published: Basel MDPI AG 01.12.2018
• Subjects: 5A70 aluminum alloy; Alloys; Aluminum alloys; Aluminum base alloys; cavity growth; Coalescing; Cold; Cold rolling; Deformation; Dislocation mobility; Dislocation pinning; fracture; Grain boundary sliding; Grain growth; Grain size; Heat treatment; High temperature; Holes; Nucleation; Strain hardening; Strain rate; Superplastic deformation; superplastic tensile; Superplasticity; Tensile tests; United States > US; China
• ISSN: 2075-4701; 2075-4701
• DOI: 10.3390/met8121065

The study of the exact physical mechanism of cavity nucleation and growth is significant in terms of predicting the extent of internal damage following superplastic deformation. The 5A70 alloy was processed by cold rolling for 14 passes with a total reduction deformation of 90% (20–2 mm) and the heat treatment was inserted at a thickness of 10 and 5 mm at 340 °C for 30 min. The superplastic tensile tests were performed at 400, 450, 500, 550 °C and the initial strain rate was 1 10−3 s−1. Cavities were observed at the head of the particle and the interface of the grain boundaries. It is suggested that the cavity was nucleated during the sliding/climbing of the dislocations, due to the precipitate pinning effect and the impeding grain boundary during grain boundary sliding (GBS). In this study, the results demonstrated a clear transition from diffusion growth to superplastic diffusion growth and plastic-controlled growth at a cavity radius larger than 1.52 and 13.90 μm. The cavity nucleation, growth, interlinkage and coalescence under the applied stress during the superplastic deformation, as well as the crack formation and expansion during the deformation, ultimately led to the superplastic fracture.