Reaction, structure and properties of eco-friendly geopolymer cement derived from mechanically activated pumice

The suitability of pumice, an altered volcanic rock, for the synthesis of geopolymer cement has been investigated. The reactivity of pumice was improved by mechanical activation (MA) in a stirred media mill for various rotor speeds (3 and 5 m/s) and residence times (ranging from 1 to 10 min), respec...

Full description

Saved in:
Bibliographic Details
Published inCeramics international Vol. 49; no. 4; pp. 6756 - 6763
Main Authors Szabó, Roland, Kristály, Ferenc, Nagy, Sándor, Singla, Rashmi, Mucsi, Gábor, Kumar, Sanjay
Format Journal Article
LanguageEnglish
Published Elsevier Ltd 15.02.2023
Subjects
Geopolymerization
Mechanical activation
Pumice
Reactivity
Stirred media mill
Stirred media mill
Reactivity
Geopolymerization
Pumice
Mechanical activation
Online AccessGet full text

Cover

More Information
Summary:The suitability of pumice, an altered volcanic rock, for the synthesis of geopolymer cement has been investigated. The reactivity of pumice was improved by mechanical activation (MA) in a stirred media mill for various rotor speeds (3 and 5 m/s) and residence times (ranging from 1 to 10 min), respectively. MA resulted into increase in specific surface area (SSA). The effect of SSA of pumice on reactivity is evident from the increase in lime adsorption capacity, which increased from 70.7 mg CaO/g solid material to 234.7 mg CaO/g solid material and the area under the calorimetric peak which increased from 4 mJ to 16.6 mJ and from 9.3 to 27.2 mJ at 27 and 60 °C aging temperatures, respectively. X-ray powder diffraction (XRD) revealed that amorphization increased up to 7% as a result of MA on the particles. Amorphous content has further increased by another 2% after geopolymerization, which can be attributed to consumption of quartz which formed reaction products. A positive correlation has been found between milling time, area under calorimetric peak and compressive strength. Geopolymer with the highest strength (13.8 MPa) was made using pumice with the highest SSA (3838 cm2/g). These results are encouraging and point to the significant potential of the use of pumice as an alternative material to develop an eco-friendly geopolymer cement that contributes toward reducing the carbon dioxide emission associated with the cement production.
ISSN:0272-8842
1873-3956
DOI:10.1016/j.ceramint.2022.10.204