High-Permeability Wood with Microwave Remodeling Structure

• Published in: Forests Vol. 12; no. 11; p. 1432
• Main Authors: Zhang, Yu, Lin, Lanying, Fu, Feng
• Format: Journal Article
• Language: English
• Published: Basel MDPI AG 01.11.2021
• Subjects: Absorption; Composite materials; Computed tomography; Cracks; Experiments; high permeability; high storage capacity; Humidity; Material absorption; Mercury; microwave puffed wood (MPW); Moisture content; Permeability; Phenolic compounds; Phenolic resins; Phenols; Plantations; Pore size; Pores; porous materials; Wood; Beijing China; China
• ISSN: 1999-4907; 1999-4907
• DOI: 10.3390/f12111432

This paper presents the development of a microwave puffed wood (MPW) with novel and unique structural features in its internal structure that are based on natural wood (NW). The focus of the research was on the comprehensive visualization of the structural characteristics of MPW from the macroscopic to the microscopic scale followed by an exploration of its impregnation capabilities. The results showed that the volume of MPW increased by about 9% compared to NW due to the presence of a large number of cracked cavities. The CT images indicated that there was a significant difference between the macroscopic cracks produced by microwave processing and the natural cracks in the wood. The mercury intrusion test results showed that macro-pores increased while the micro-pores decreased in the MPW compared to in the NW. The MPW showed good fluid permeability and liquid absorption performance. The phenolic resin penetration rate of the MPW was about 20 times that of the NW, and the material absorption was more than 2 times that of the NW. The crack space enabled the MPW to serve as a fluid transportation and a storage warehouse. MPW is a super container based on natural materials. It has broad potential in more fields, such as in wood composite materials.