Research on Gluing Properties of Thick Bamboo-Wood-Oriented Strand Boards

• Published in: Forests Vol. 14; no. 10; p. 2094
• Main Authors: Yang, Bajin, Guo, Xu, Chen, Wu, Wang, Xingyu, Du, Guanben, Dong, Chunlei
• Format: Journal Article
• Language: English
• Published: Basel MDPI AG 01.10.2023
• Subjects: Absorption; Adhesives; Bamboo; bonding interface; bonding performance; Bonding strength; BWOSB; Chemical properties; Cunninghamia lanceolata; Damage; Dry density; Evaluation; Gluing; Hardwoods; Hot pressing; Isocyanates; Mechanical properties; Modulus of elasticity; Modulus of rupture; Moisture content; Physical properties; Raw materials; Shear strength; Strands; Swelling; Temperature; Thickness; Water absorption; Wood; China
• ISSN: 1999-4907; 1999-4907
• DOI: 10.3390/f14102094

This study investigated the effects of adhesive resination and bamboo strand content on the physical and mechanical properties of thick Bamboo-Wood-oriented strand board (BWOSB), such as the air dry density (ADD), internal bond strength (IB), water absorption thickness swelling (TS), modulus of rupture (MOR), modulus of elasticity (MOE), and gluing properties. The raw materials used included large strands prepared from Chinese fir (Cunninghamia lanceolata), bamboo (Phyllostachys edulis), and modified isocyanate resin (PMDI). In this study, BWOSB specimens with different adhesive resination and bamboo strand content were fabricated, and their physical–mechanical properties were examined. It was found that the physical and mechanical properties of BWOSB with 8% PMDI resination were better than those with 5%, and their gluing damage was mostly in the form of the tearing of the raised vascular bundles of bamboo strands and the wood-breaking damage of wood strands. With the increase in the proportion of bamboo strands, the internal bonding strength and the short-span shear strength of BWOSB showed a tendency to decrease at first and then increase. The swelling rate of the water absorption thickness showed a tendency to decrease, and the other properties of BWOSB did not show a clear correlation with the change in the proportion of bamboo strands. The unique gluing interface between the bamboo and wood strands, which either used the “keyway” type of gluing effect or the “nail” type of gluing effect, determined the gluing performance of BWOSB, and the proportion of bamboo and wood strands influenced the gluing interface and gluing type of BWOSB, which ultimately affected the gluing performance of BWOSBs. The proportion of bamboo and wood strands also affected the gluing properties of BWOSBs by influencing the gluing interface and gluing type. This study provides a reference for the development of the production process of thick BWOSB and its application in the field of heavy load construction.