Influence of Dopants on Structure of Polycrystalline Bismuth Niobate
Bismuth niobate (BiNbO ) has attracted attention as a low-fired ceramics with promising microwave application potential. BiNbO ceramics was fabricated by mixed oxide method and sintered at temperature <1000°C. As the sintering aids a small amount of CuO oxide was used. The crystalline structure o...
Saved in:
Published in | Advances in materials science Vol. 18; no. 4; pp. 35 - 41 |
---|---|
Main Authors | , |
Format | Journal Article |
Language | English |
Published |
Gdansk
Sciendo
01.12.2018
De Gruyter Poland |
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | Bismuth niobate (BiNbO
) has attracted attention as a low-fired ceramics with promising microwave application potential. BiNbO
ceramics was fabricated by mixed oxide method and sintered at temperature
<1000°C. As the sintering aids a small amount of CuO oxide was used. The crystalline structure of the ceramic samples was examined by X-ray diffraction method at room temperature. The Rietveld refinement method was used for analysis of diffraction data. As a result an influence of dopants on crystal structure of bismuth niobate (BiNbO
) ceramics was revealed. It was found that fabricated BiNbO
ceramics adopted the orthorhombic symmetry (
-BiNbO
phase,
(52) space group). Small differences in elementary cell parameters were found. |
---|---|