Evaluation of the Effect of Glow Discharge Plasma Surface Treatment on Bonding Cements to Zirconia

• Published in: The open dentistry journal Vol. 12; no. 1; pp. 846 - 855
• Main Authors: Binmahfooz, Abdulelah M, Basunbul, Ghadeer I, ArRejaie, Aws S
• Format: Journal Article
• Language: English
• Published: United Arab Emirates Bentham Open 01.01.2018
• Subjects: Dentistry; Zirconia; Cohesive failure; Glow discharge plasma; Bonding cement; Y-TZP ceramics; Adhesive failure
• ISSN: 1874-2106; 1874-2106
• DOI: 10.2174/1874210601812010846

The major difference in the chemical composition of Y-TZP ceramics, as compared with conventional porcelain, led researchers to develop alternative solutions for achieving durable and long term bonding with the zirconia surface. The study aims to evaluate the effects of glow discharge treatment on the bonding between cement and zirconia. The zirconia rings and rods were prepared with the Zirconia Y-TZP powder and TZ-3YSB-E (Tosoh-Zirconia) through auto-mix to investigate the glow discharge and thermo-cycling. An orientation Teflon mold was used to centralize each rod into the zirconia ring, and aided as a cementation jig during the cementation procedure. Cohesive failure (2/3 or more of luting agent remained on the zirconia surface) has been majorly observed with RelyX Ultimate, while adhesion failure (less than 1/3 of the luting agent remained on the zirconia surface) has been primarily observed in Ketac-Cem. Mixed failure was observed among the three specimen including Rely X Unicem 2, Multilink Auto-mix and Ceramir. The glow discharge surface treatment procedure had a major impact on bond strength to zirconia.