Integrated utilization of high alumina fly ash for synthesis of foam glass ceramic

• Published in: Ceramics international Vol. 44; no. 12; pp. 13681 - 13688
• Main Authors: Wang, Hao, Chen, Ziwei, Ji, Ru, Liu, Lili, Wang, Xidong
• Format: Journal Article
• Language: English
• Published: Elsevier Ltd 15.08.2018
• Subjects: Building insulation materials; Foam glass ceramic; High alumina fly ash; Waste glass; Foam glass ceramic; High alumina fly ash; Building insulation materials; Waste glass
• ISSN: 0272-8842; 1873-3956
• DOI: 10.1016/j.ceramint.2018.04.207

Due to the numerous increase of the building energy consumption and huge volume of industrial wastes produced in China, the development of thermal insulation materials is quite needed. Herein, foam glass ceramic, a kind of thermal insulation materials, was fabricated by using solid wastes high alumina fly ash and waste glass as the main raw materials. First, in this study the proportion scheme of this research was designed by using Factsage 7.1 and the foaming agent was CaSO4. Secondly, the decomposition of calcium sulfate and the influence of process parameters, namely the sintering temperature and the foaming agent additive amount, on the microstructure and mechanical properties of foam glass ceramic were investigated. The experimental results showed that when the proposed foam glass ceramic was sintered at between 1180 and 1220 °C, it exerted excellent macro and micro properties. The optimum parameters were 2% CaSO4 addition and sintering temperature of 1200 °C, and the corresponding bulk density and compress strength values were 0.98 g/cm3 and 9.84 MPa, respectively. Overall these results indicated that the preparation of foam glass ceramic made up a promising strategy for recycling industrial waste into new kind of building insulation materials.