Modification induced by gamma irradiation in Bayfol CR 1-4 polycarbonate

• Published in: Radiation effects and defects in solids Vol. 168; no. 4; pp. 286 - 296
• Main Authors: Nouh, S. A., Bahareth, Radiyah A.
• Format: Journal Article
• Language: English
• Published: Abingdon Taylor & Francis 01.04.2013; Taylor & Francis Ltd
• Subjects: Bayfol; Crosslinking; Decomposition; Degradation; Diffraction; Fourier transforms; gamma; Gamma irradiation; Gamma rays; Irradiation; Polycarbonates; Polymers; Spectroscopy; structural properties; TGA; Thermogravimetric analysis; V-I characteristics; Viscosity
• ISSN: 1042-0150; 1029-4953
• DOI: 10.1080/10420150.2012.761991

Bayfol CR 1-4 polycarbonate is a class of polymeric solid state nuclear track detector which has many applications in various radiation detection fields. Samples from sheets of Bayfol have been irradiated with gamma doses ranging from 100 to 620 kGy. The structural modifications in the gamma-irradiated Bayfol samples have been studied as a function of dose, using different characterization techniques such as X-ray diffraction (XRD), Fourier-transform infrared (FTIR) spectroscopy, intrinsic viscosity and refractive index. The results indicate that the carbonyl group (C˭O) degraded under irradiation up to 200 kGy. This degradation, reported by FTIR spectroscopy enhanced the degree of ordering in the degraded samples as revealed by the XRD technique. Above 200 and up to 620 kGy, cross-linking is achieved, leading to an increase in the intrinsic viscosity from 0.41 to 0.78 at 35°C, indicating an increase in the average molecular mass. On the other hand, the resultant effect of gamma irradiation on the thermal properties of Bayfol has been investigated using thermo-gravimetric analysis, results indicating that the gamma irradiation in the dose range 200-620 kGy led to a more compact structure of Bayfol polymer, which resulted in an improvement in its thermal stability with an increase in the activation energy of thermal decomposition due to cross-linking. In addition, the V-I characteristics of the polymer samples were performed, results indicated that at higher voltage, the conduction mechanism of Bayfol CR 1-4 was identified as the Poole-Frenkel type.